Abstract：Stainless steel powder was prepared by high pressure water atomization method. The influences of nozzle diameter and water pressure on the morphology, oxygen content, particle size distribution and tap density of powder were investigated. The microstructure and properties of samples were characterized by means of laser particle size analyzer, scanning electronic microscope, etc. The results indicate that, the stainless steel powder has small average particle size ([D50] is 8.83 μm, [D90] is 20.80 μm), uniform particle size distribution, low oxygen content and high tap density when the water pressure is 115 MPa and the nozzle diameter is 3.5 mm.
冷 丹，曾克里，王志勇，宋信强，朱 杰，田学娜. 高压水雾化法制备MIM不锈钢粉末工艺研究[J]. , 2015, 25(02): 8-11.
LENG Dan, ZENG Ke-li, WANG Zhi-yong, SONG Xin-qiang, ZHU Jie, TIAN Xue-na. Study on the preparation process of MIM stainless steel powder by high pressure water atomization method. , 2015, 25(02): 8-11.
[1] 章欣．316L不锈钢粉末注射成型工艺研究[D]．沈阳，沈阳理工大学，2012．[2] 于朝清，徐永红，章应，等．金属雾化制粉技术现状[J]．电工材料，2010，2：9-17．[3] 欧阳鸿武， 陈欣， 余文寿，等．气雾化制粉技术发展历程及展望[J]．粉末冶金技术，2007，25(1)：53-58．[4] LI Songlin，YANG Qiumin，CUI Jianmin，et al．Effects of major impurity elements on compressibility of water-atomized iron powder [J]．Powder Metallurgy and Metal Ceramics，2012，51(3-4)：142-149．[5] SURI Pavan，KOSESKI Ryan P，GERMAN Randall M．Microstructural evolution of injection molded gas-and water-atomized 316L stainless steel powder during sintering [J]．Materials Science and Engineering：A，2005，402(1-2)：341-348．[6] 李松林，孙云飞，张传福，等．金属注射成形气雾化和水雾化316L不锈钢耐蚀性[J]．粉末冶金材料科学与工程，2005，10(5)：309-313．[7] 麻洪秋，贾成厂，金成海，等．急冷水雾化工艺对金属粉末性能的影响[J]．粉末冶金技术，2002，20(6)：346-349．[8] 黄圣坤，余勇，曾归余，等．金刚石工具用FeCu30预合金粉末水雾化工艺的研究[J]．金刚石与磨料磨具工程，2012，32(5)：39-41．[9] 解传娣，陈文．水雾化Cu-0.3La预合金粉制备工艺研究[J]．粉末冶金技术，2012，29(4)：279-282．[10] 段柏华，曲选辉，林冰涛，等．MIM用金属粉末的现状及发展[J]．粉末冶金工业，2008，18(4)：31-35．
2015, Vol. 25 