Effect of hot extrusion on properties of SiC/2024Al composites
HU Zhi-yong1,YAN Li-peng2,WANG Ai-qin3
1. China Airborne Missile Academy, Luoyang 471099, China 2. School of Material and Engineering, He’nan Mechanical and Electrical Engineering College, Xinxiang 453003, China 3. School of Material Science and Engineering, He’nan University of Science and Technology, Luoyang 471099, China
Abstract：The 35%SiC/2024Al (mass percent) composite was prepared by cold pressing and sintering, and then the specimen was hot-extruded. The microstructure of the material was observed by optical microscope and TEM, the physical and mechanical properties were also tested. The distribution characteristic of SiC particles, change of grains in matrix and the strengthening mechanism of the composite were investigated. The results show that the distribution of SiC particles is more uniform and the segregation decreases after hot-extrusion. The arrangement of SiC particles in the direction of extrusion is more oriental and orderly. The grains of the composite are refined. The densities and tensile strength are increased significantly after hot-extrusion.
户志勇，兖利鹏，王爱琴. 热挤压对SiC/2024Al复合材料性能的影响[J]. , 2015, 25(04): 26-29.
HU Zhi-yong,YAN Li-peng,WANG Ai-qin. Effect of hot extrusion on properties of SiC/2024Al composites. , 2015, 25(04): 26-29.
2015, Vol. 25 