Abstract：The excellent performance and research progress of vanadium carbide powders at home and abroad were summarized. Four main preparation methods (carbothermal reduction, gas phase reduction, precursor and mechanical alloying methods) for vanadium carbide powders were introduced in detail. The advantages, disadvantages and the latest research progress of each preparation method were also introduced. Finally, the development prospects of vanadium carbide nanopowders were prospected.
胡文萌，赵志伟，陈飞晓，王明超. 纳米碳化钒粉末制备的研究现状[J]. , 2015, 25(06): 62-65.
HU Wen-meng,ZHAO Zhi-wei,CHEN Fei-xiao,WANG Ming-chao. Research status on preparation of vanadium carbide nanopowder. , 2015, 25(06): 62-65.
[1] Didziulis S V, Butcher K D. A perspective on the properties and surface reactivities of carbides and nitrides of titanium and vanadium[J]. Coordination Chemistry Reviews, 2013, 257 (1): 93-109.[2] Sun Z M, Ahuja R, Lowther J E. Mechanical properties of vanadium carbide and a ternary vanadium tungsten carbide[J]. Solid State Communications，2010，150 (15-16): 697-700.[3] Lei M, Zhao H Z, Yang H, et al. Synthesis of transition metal carbide nanoparticles through melamine and metal oxides[J]. Journal of the European Ceramic Society, 2008, 28(8):1671-1677.[4] Mahajan M, Singh K, Pandey O P. Single step synthesis of nano vanadium carbide-V8C7 phase[J]. Journal of Refractory Metals and Hard Materials, 2013, 36 (1): 106-110.[5] 李良彬，钟毓茂. 碳化钒作为碳源合成金刚石[J]. 高压物理学报，1998，12(2): 141-144.[6] Neylon M K, Choi S, Kwon H, et al. Catalytic properties of early transition metal nitrides and carbides: n-butane hydrogenolysis, dehydrogenation and isomerization[J]. Applied Catalysis A: General, 1999, 183(2): 253-263.[7] Bock A, Schubert W D, Lux B. Inhibition of grain growth on submicron cemented carbides[J]. Powder Metallurgy International, 1992, 24(1): 20-26.[8] 吴其山. 超细WC- Co硬质合金研究综述[J]. 中国钨业，2005，20（6）：35-40.[9] 孙景，刘俊朋，郭小南. 含VC 的WC-10%Ni硬质合金无磁机理研究[J]. 硬质合金，2003，20(2): 72-75.[10] 张丽英，吴成义，宴洪波. 含钒超细晶粒WC－(Ni-Fe)系硬质合金复合粉的研制[J]．金属 学报，1999，35(2): 155-158.[11] Da Silva A G P , Schubert W D, Lux B. The role of the binder phase in the WC- Co sintering[J]. Materials Research, 2001, 4 (2): 59-62.[12] Union Carbide Corporation. Process for the preparation of fine grain metal carbide powders:US, 3932594[P]. 1973-12-28.[13] 黄道鑫. 提钒炼钢[M]. 北京: 冶金工业出版社, 2000.[14] 陈厚生．碳化钒与氮化钒[J] . 钢铁钒钛，2000，21(1): 70-71.[15] 汤仁中. 碳化钒的研制[J] . 稀有金属与硬质合金，2000，141(4): 11-13.[16] Choi K, Hwang N M. Effect of VC addition on microstructural evolution of WC-Co alloy: mechanism of grain growth inhibition[J]. Powder Metallurgy, 2000, 43(2):168-172.[17] 吴恩熙.，颜练武，胡茂中. 氧化钒制取碳化钒的热力学分析[J]. 硬质合金，2004，21(1)：1-3.[18] 姜中涛，李力懈，陈巧旺. 常压下碳热还原制备碳化钒(V8C7)粉末的研究[J]. 硬质合金，2011，28(5): 294-299.[19] 吴恩熙，颜练武，钱崇梁. 纳米V8C7粉末的制备[J]. 中南大学学报(自然科学版)，2005，36(5)：771-776.[20] Dai L Y, Lin S F, Chen J F, et al. A new method of synthesizing ultrafine vanadium carbide by dielectric barrier discharge plasma assisted milling[J]. International Journal of Refractory Metals and Hard Materials, 2012, 30 (1): 48-50.[21] 姜中涛，叶金文，刘颖，等. 碳热还原法制备V8C7粉末的研究[J]. 功能材料，2009，40(5): 820-822.[22] Kapoor R, Oyama S T. Synthesis of vanadium carbide by temperature programmed reaction[J]. Journal of Solid State Chemistry, 1995, 120 (2): 320-326.[23] Choi J G, Ha J, Hong J W. Synthesis and catalytic properties of vanadium interstitial compounds[J]. Applied Catalysis A: General, 1998, 168 (1): 47-56. [24] 吴恩熙, 颜练武, 钱崇梁. 碳化钒粉末的制备方法：中国，200310101104.3[P]. 2003-10-15[25] Sadangi RK, McCandlishLE, Kear BH, et al. Synthesis and characterization of submicron vanadium and chromium carbide grain growth inhibitors[A]. In:Oakes J, Reinshagn JH. Advances in Powder Metallurgy & Particulate Materials(Part 1)[C]. Princeton: MPIF, 1998. 9-15.[26] 赵志伟，刘颖，朱贺，等. 反应温度对纳米碳化钒(V8C7)制备的影响[J]. 粉末冶金工业，2009，19(5)：37-41.[27] Zhao Z W, Liu Y, Cao H, et al. Phase evolution during synthesis of vanadium carbide (V8C7) nanopowders by thermal processing of the precursor[J]. Vacuum, 2008, 82 (8): 852-855.[28] Zhao Z W, Liu Y, Cao H, et al. Synthesis of vanadium carbide nanopowders by thermal processing and their characterization[J]. Powder Technology, 2008, 181 (1): 31-35.[29] Lin H, Tao B W, Li Q. In situ synthesis of V8C7 nanopowders from a new precursor[J]. Journal of Refractory Metals and Hard Materials, 2012, 31 (3):138-140. [30] Ye J W, LiuY, Zhao Z W, et al. Synthesis of VC nanopowders by thermal processing of precursor with CaF2 addition[J]. Journal of Alloys and Compounds, 2010, 496 (1-2):278-281.[31] 张斌．机械合金化方法制备碳化物的研究[D]．浙江大学，2005.[32] 高海燕，曹顺华. 机械合金化制备纳米晶硬质合金粉的进展[J]. 粉末冶金技术，2003，21( 6): 355-358.[33] 程凤军，王一三，赖丽，等. 原位生成超细 VC颗粒增强铁基复合材料[J]. 钢铁钒钛，2005，26(2):58-61.[34] 于三三，杨灿，李双明，等. V2O3碳热还原法制备VC过程的研究[J]. 硬质合金，2011，28(2):78-82.[35] Zhang B, Li Z Q. Synthesis of vanadium carbide by mechanical alloying[J]. Journal of Alloys and Compounds, 2005, 392 (1-2):183-186.[36] ChenY J, Zhang H, Ye H N, et al. A simple and novel route to synthesize nano-vanadium carbide using magnesium powders, vanadium pentoxide and different carbon source[J]. International Journal of Refractory Metals and Hard Materials, 2011, 29(4):528-531.[37] Hossein-Zadeh M, Mirzaee O. Synthesis and characterization of V8C7 nanocrystalline powder by heating milled mixture of V2O5, C and Ca via mechanochemical activation[J]. Advanced Powder Technology, 2014, 25(3):978-982.
2015, Vol. 25 