Effect of dispersant on the preparation of sub-micron spherical SiO2 particles
LIU Wan-bin1,SHAO Hui-ping2,HUANG Xiao-hong2,ZHENG Hang2
（1. Taizhou Cosmos Engineering Consulting Ltd., Taizhou 318000, China 2. Institute for Advanced Materials and Technology, University of Science and Technology Beijing,Beijing 100083, China）
Abstract：The monodisperse submicron silica microspheres were successfully prepared by sol-gel method. Ammonia was used as catalyst, mixture of alcohol and water was employed as solvent, and silane coupling agent was used as surfactant. The influence of silane coupling agent dosage and the order added to the solution on particle size were studied. The morphology of the particles was characterized by scanning electron microscope （SEM）. The experimental results show that, under the reaction temperature of 20 ℃, ethyl orthosilicate concentration of 0.2-0.3 mol/L, and the dispersant of 0.075-0.125 mL added after the incubation reaction, the silica microspheres of 300-600 nm are prepared. And at room temperature of 20 ℃, ethyl orthosilicate concentration of 0.3 mol/L, 0.075-0.125 mL dispersant added after the incubation reaction, the silica particles grow up more easily to silica microspheres of about 600 nm.
收稿日期: 2015-07-23
出版日期: 2015-12-08
基金资助:广东产学研结合资助项目
通讯作者:
邵慧萍
E-mail: shaohp@ustb.edu.cn
引用本文:
刘万斌，邵慧萍，黄小泓，郑 航. 分散剂对亚微米级球形SiO2微粒制备的影响[J]. , 2015, 25(06): 14-17.
LIU Wan-bin,SHAO Hui-ping,HUANG Xiao-hong,ZHENG Hang. Effect of dispersant on the preparation of sub-micron spherical SiO2 particles. , 2015, 25(06): 14-17.
2015, Vol. 25 