Abstract：Polytetrafluoroethylene (PTFE) composites filled with wollastonite fiber (WF) and molybdenum?disulfide (MoS2) were prepared through powder metallurgy. The influence of WF content on the tensile strength， hardness， friction and wear properties of the WF- MoS2/PTFE composites were investigated. The friction surface was observed by scanning electron microscope (SEM). The results show that the hardness increases， and the elongation at break reduces about 70% than pure PTFE by filling with the WF and MoS2. Tensile strength of the composite decreases gradually when mass percent of WF is more than 7%. The friction coefficient of the composite increases rapidly and the wear loss further decreases with addition of WF. The investigation of SEM indicates that WF on the friction surface gives priority to the load， the friction between PTFE matrix and dual surface is reduced， thus the wear loss is decreased. MoS2 particles are easy to wear， and its fragment has lubrication effect. PTFE filling with 18% MoS2 and 7% WF (mass percent) has a relative lower friction coefficient and wear loss.
[1] 钱知勉，包永忠.氟塑料加工与应用[M]. 北京：化学工业出版社，2010
[2] 应伟斌.填充改性增强PTFE复合材料的力学性能研究[D]. 江苏：江苏大学，2006
[3] Zhen Zuo，Laizhou Song，Yulin Yang.Tribological behavior of polyethersulfone-reinforced polytetrafluoroethylene composite under dry sliding condition [J][J]., 2015, 86:17-27
[4] J T Shen，M Top，Y T Pei，et al.[J]., 2015, 322-323:171-180
[5]解挺，杨华平，江凯.数值模拟填料含量对复合材料摩擦性能的影响[J].复合材料学报, 2015, 32(1):39-46
[6] H Unal，A Mimaroglu，U Kadioglu.[J]., 2004, 25(3):239-245
[7]禹权, 叶素娟.硅灰石纤维改性材料摩擦性研究[J].工程塑料应用, 2012, 40(4):73-75
[8] V N Aderikha，A P Krasnov，V A Shapovalova，et al.Peculiarities of tribological behavior of low-filled composites based on polytetrafluoroethylene (PTFE) and molybdenum disulfide [J][J]., 2014, (320):135-142
[9]G O Sirenko，L Ya Midak.Effects of a solid lubricant and technological parameters on the friction wear and mechanical properties of a composite based on polytetrafluoroethylene powder[J].Powder Metallurgy and Metal Ceramics, 2006, 45(5-6):230-238
[10]R K Goyal，M Yadav.Study on wear and friction behavior of graphite flake-filled PTFE composites[J].Journal of Applied Polymer Science, 2013, 127(4):3186-3191
[11]路琴，张静，何春霞.混杂填料增强复合材料的摩擦学性能研究[J].塑料, 2008, 37(3):15-17
[12]王齐华，宁丽萍，杨景锋，等.碳纤维及石墨填充复合材料的摩擦学性能研究[J].材料科学与工程学报, 2004, 22(5):705-708
[13]徐红星，袁新华，程晓农，等.碳纤维玻璃纤维石墨协同改性复合材料力学性能[J].润滑与密封, 2007, 32(9):88-90
[14] Jaydeep Khedkar，Ioan Negulescu，Efstathios I Meletis.Sliding wear behavior of PTFE composites [J][J]., 2002, 252(5-6):361-369
[15]孙庆杰，冯新，王海棠，等.硅灰石的表面改性对其填充复合材料摩擦学性能和力学性能的影响[J].工程塑料应用, 2008, 36(8):13-16
[16] American Society for Testing and Materials.ASTM D4894-07 Standard Specification for Polytetrafluoroethylene (PTFE) Granular Molding and Ram Extrusion Materials[S]. West Conshohocken，United States：American Society for Testing and Materials International，2012.
2016, Vol. 26 