Abstract：TC11 alloy samples were prepared by selective laser melting technology. The influence of laser parameters and laser scanning strategy on the forming properties of TC11 alloy was investigated. The results indicate that， with the increase of laser scanning speed， the metal spherical particles adhering to the alloy surface increase， the width of single scanning molten pool decrease， and the surface of the sample becomes much coarser. There are spherical pores exist in the sample when the laser scanning speed is 0.6 m/s， while there are irregular pores exist in the sample when the laser scanning speed is greater than 1.2 m/s. With the increase of laser power， the width of single scanning molten pool increase and the surface of the samples become much smoother. There are little small irregular pores inside the sample when the laser power is not higher than 280 W， while there are little small spherical pores inside the sample when the laser power is 320 W. The scanning strategy of each layer is rotated 67 degrees relative to the previous layer makes up for the height difference between the center and edge caused by the previous scanning layer， avoiding the height difference increase， thus avoiding the internal porosity. The research provides a basis for selecting appropriate laser parameters and scanning strategy for preparing TC11 alloy by selective laser melting.
[1] Wong K V，Hernandez A.A Review of Additive Manufacturing[J].ISRN Mechanical Engineering, 2012, 2012:1-10
[2]Yadroitsev I，Smurov I.Selective laser melting technology: From the single laser melted track stability to 3D parts of complex shape[J].Physics Procedia, 2010, 5:551-560
[3]Yadroitsev I，Thivillon L，Bertrand P，Smurov I.Strategy of manufacturing components with designed internal structure by selective laser melting of metallic powder[J].Applied Surface Science, 2007, 254:980-983
[4]Strano G，Hao L，Everson R M，Evans K E.Surface roughness analysis modelling and prediction in selective laser melting[J].Journal of Materials Processing Technology, 2013, 213:589-597
[5]J P Krutha，L Froyenb，J Van Vaerenbergha，P Mercelisa，M Romboutsb，B Lauwersa. Selective laser melting of iron-based powder[J].Journal of Materials Processing Technology, 2004, 149:616-622
[6] E O Olakanmi，R F Cochrane，K W Dalgarno.A review on selective laser sintering / melting (SLS/SLM) of aluminium alloy powders:Processing microstructure and properties[J].Progress in Materials Science, 2015, 74:401-477
[7] Shishkovsky I，Yadroitsev I，Smurov I.Direct selective laser melting of nitinol powder[J].Physics Procedia, 2012, 39:447-454
[8]Lai-Chang Zhang，Hooyar Attar.Selective Laser Melting of Titanium Alloys and Titanium Matrix Composites for Biomedical Applications: A Review[J].Advanced engineering materials, 2016, 18(4):463-475
[9] Jayasheelan Vaithilingama，Samuel Kilsbyb，Ruth D Goodridgea，Steven D R Christieb，Steve Edmondsonc，Richard J M Haguea.Immobilization of an antibacterial drug to Ti6Al4V components fabricated using selective laser melting[J].Applied Surface Science, 2014, 314:642-654
[10]张霜银，林鑫，陈静，黄卫东.热处理对激光成形TC4合金组织及性能的影响[J].稀有金属材料科学与工程, 2017, 36(7):1263-1266
[11]颜茜，舒鑫柱，祝菲霞，孙坤.TC11钛合金4种典型组织静态力学性能对比研究[J].云南大学学报自然科学版, 2016, 38(1):99-104
[12]何博文，冉先喆，田象军，王华明.激光增材制造TC11钛合金的耐蚀性研究[J].中国激光, 2016, 43(4):0403001-1
[13]Dongdong Gu，Yifu Shen.Balling phenomena in direct laser sintering of stainless steel powder: Metallurgical mechanisms and control methods[J].Materials and Design, 2009, 30:2903-2910
2018, Vol. 28 