Study on the microstructure and properties of multi-component hard phase reinforced Mo2FeB2 based cermets
TAO Ze-xu，CONG Shan-hai，PENG Jia-jian，WANG Xiao-feng
（Key Laboratory of Ferrous Metallurgy and Resources Utilization， Ministry of Education， Wuhan University of Science and Technology， Wuhan 430081，China）
Abstract：Mo2FeB2 based cermets were prepared by vacuum liquid phase sintering process using Mo， FeB and Fe powder as raw materials and adding various contents of WC， NbC， TiC. The effects of multi-component hard phase on the microstructure and properties of samples were studied by metallographic microscope， scanning electron microscope， energy spectrum analysis， X-ray diffraction， rockwell hardness test and wear test. The results show that the multi-component hard phase addition can refine the microstructure and dispersion strengthening， thus improving the hardness and wear resistance of cermets. When the mass percent of WC， NbC and TiC is 10%， 4% and 5%， respectively， the hardness and wear resistance of the samples are the highest.
陶则旭，从善海，彭家健，王晓峰. 多组元硬质相增强Mo2FeB2基金属陶瓷的组织和性能研究[J]. , 2018, 28(03): 44-47.
TAO Ze-xu，CONG Shan-hai，PENG Jia-jian，WANG Xiao-feng. Study on the microstructure and properties of multi-component hard phase reinforced Mo2FeB2 based cermets. , 2018, 28(03): 44-47.
[1]Takagi K I.Development and application of high strength ternary boride base cermets[J].Cheminform, 2006, 37(179):2809-2818
[2]Zhuang M A, Wei W, Zou J F, et al.Preparation and properties of flame-sprayed Mo-FeB-Fe cermet coatings[J].Transactions of Nonferrous Metals Society of China, 2011, 21(6):1314-1321
[3]曾鲜, 郭志猛, 刘祥庆, 等.基新型硬质合金的制备[J].粉末冶金工业, 2013, 23(1):32-36
[4]Yu H, Zheng Y, Liu W, et al.Effect of V content on the microstructure and mechanical properties of Mo2FeB2,based cermets[J].International Journal of Refractory Metals & Hard Materials, 2010, 31(5):2680-2683
[5] 胡梅, 从善海, 张志伟.WC增强Mo_2FeB_2基金属陶瓷的组织与性能研究[J]. 稀有金属与硬质合金, 2015(4):29-33.[J].稀有金属与硬质合金, 2015, 43(4):29-33
[6]张志伟, 从善海, 胡梅.含量对基金属陶瓷的显微组织和力学性能的影响[J].粉末冶金工业, 2015, 25(5):52-55
[7] 章晓波.含不同第二相碳化物Ti(C, N)基金属陶瓷的显微组织和切削性能研究.[J].硬质合金, 2007, 24(4):251-251
2018, Vol. 28 