Study on preparation of copper-base tee parts by warm flow compaction
YANG Yi1，DING Tao1，NI Dong-hui2
（1. School of Mechanical Engineering， Hubei Engineering University， Xiaogan 432000， China 2. Guangdong Key Laboratory for Advanced Metallic Materials Fabrication and Forming， School of Mechanical & Automotive Engineering， South China University of Technology， Guangzhou 510640， China）
Abstract：The near net-shape manufacturing process of complex parts is always the development goal of warm flow compaction technology. The copper-based powder material was used as the research object， and the tee part green body was pressed at 85 ℃ by using the warm flow compaction process. Through a reasonable degreasing and sintering process， the tee part sample was successfully prepared. The degreasing process， microstructure and density of the sample were also analyzed. Results show that the copper-based tee sintered part without significant surface defects is obtained by keeping the temperature at 300 ℃ and 450 ℃ for 30 min respectively and slowly heating to 950 ℃ for sintering for 60 min. However， the parts density distribution is not uniform after sintering， and the lateral part density is significantly lower than the axial part.
杨 义，丁 涛，倪东惠. 铜基粉末材料流动温压成形三通管的实验研究[J]. , 2018, 28(04): 37-41.
YANG Yi，DING Tao，NI Dong-hui. Study on preparation of copper-base tee parts by warm flow compaction. , 2018, 28(04): 37-41.
［1］Veltl G,Oppert A,Petzoldt F. Warm Flow Compaction fosters more complex PM parts[J]. Metal Powder Report, 2001, 56(2)：26-28.［2］Ngai T L ,Zhou Shuibo ,Xiao Z Y. et al. Debinding and sintering of warm compacted and binder-treated complex iron-base part[J]. Transaction of Nonferrous Metals Society of China ,2007(17): 589-593.［3］Xiao Z Y,wang J, Ngai T L, et al. Study on warm flow compacted tungsten-based alloy powder for cross-shape part[J]. Materials Science Forum,2008,561/562:921-924.［4］王建强,李国民,赵洪波.烧结工艺对铜基粉末冶金摩擦材料的影响[J].润滑与密封,2013,38(10):77-79.[5]胡昌旭,倪东惠,谭文昌等.流动温压制备不锈钢十字件的试验研究[J].粉末冶金技术,2010,28(4):284-287.[6]Liu S Y. The application and exploitation in copper industry production[J]. The nonferrous metals metallurgy of Xinjiang, 1995, 23(1): 38-42.[7] German R M. Sintering Theory and Practice[M]. New York: John Wiley and Sons, Inc, 1996.110.
2018, Vol. 28 