Abstract:A modified zirconium-containing layer was prepared on the surface of 0Cr19Ni9N stainless steel by double glow plasma alloying technique using 705 zirconium plate as source material. The microstructure and hardness of zirconium infiltrated layer were analyzed, and the friction and wear properties of zirconium infiltrated sample were tested under dry friction test conditions. The results show that a compact and uniform zirconium-containing modified layer forms on the surface of 0Cr19Ni9N stainless steel after plasma alloying. The modified layer protects the matrix steel, improves the matrix strength and its friction and wear properties.
收稿日期: 2018-01-15
出版日期: 2018-12-24
通讯作者:
黄敏
E-mail: 279934827@qq.com
引用本文:
黄 敏. 元素锆等离子渗入0Cr19Ni9N不锈钢及其摩擦磨损性能研究[J]. , 2018, 28(06): 52-55.
HUANG Min. Study on plasma infiltration of elemental Zr into 0Cr19Ni9N stainless steel and its friction and wear properties. , 2018, 28(06): 52-55.