Abstract:NiO components were doped to TiO2 carrier of V2O5-WO3/TiO2 catalysts by co-precipitation and the effect of NiO content on the microstructure, surface properties and SCR performance of the catalyst were investigated. Results show that NiO is incorporated into TiO2 to form NiTiO3, which inhibits the growth of TiO2 grains. The presence of isolated tetrahedron VO4 in Ni3V2O8 reduces the Br?nsted acid content on the catalyst surface, while the interaction between NiOx and VOx reduces the reducibility of the catalyst. The existence of V4+ in Ni3V2O8 is also not conducive to the improvement of catalyst denitration activity. Therefore, NiO doping into V2O5-WO3/TiO2 catalysts by an inappropriate method tends to poison the catalysts.
[1] 任超, 任晓光, 宋永吉. 焙烧条件对NiO/TiO2催化剂结构和脱硝性能的影响[J]. 工业催化, 2011, 19(1): 23-26.[2] Yuan D L, Li X Y, Zao Q D. Preparation and characterization of Ni-Ti-O mixed oxide for selective catalytic reduction of NO under lean-burn conditions[J]. Chinese Journal of Catalysis, 2013, 34(7): 1449-1455.[3] Zhang Q M, Song C L, Lv G, Bin F, Pang H T, Song J O. Effect of metal oxide partial substitution of V2O5 in V2O5-WO3/TiO2 on selective catalytic reduction of NO with NH3. Journal of Industrial and Engineering Chemistry, 2015, 24: 79-86.[4] 余艳, 袁博, 周松. NH3-SCR钒系催化剂的制备及脱硝性能研究[J]. 车用发动机, 2015, 3: 37-40.[5] Yu J C, Lin J , Kwok R W M. Ti1-xZrxO2 solid solutions for the photocatalytic degradation of acetone in air[J]. J phys chem B, 1998, 102(26): 5094-5098.[6] Peng Y, Li K, Li J. Identification of the active sites on CeO2-WO3 catalysts for SCR of NOx with NH3: An in situ IR and Raman spectroscopy study[J]. Applied Catalysis B Environmental, 2013, 140-141(2): 483-492.[7] Emeis C A. Determination of integrated molar extinction coefficients for IR absorption bands of pyridine adsorbed on solid acid catalysts[J]. Journal of Catalysis, 1993, 141:347-354.[8] Lietti L, Alemany J L, Forzatti P, et al. Reactivity of V2O5-WO3/TiO2 catalysts in the selective catalytic reduction of nitric oxide by ammonia[J]. Catalysis Today, 1996, 29(1): 143-148.[9] Eckert H, Wachs I E. Solid-state vanadium-51 NMR structural studies on supported vanadium(V) oxide catalysts: vanadium oxide surface layers on alumina and titania supports[J]. Journal of Physical Chemistry, 1989, 93(18): 6796-6805.[10] Alemany L J, Lietti L, Ferlazzo N, et al. Reactivity and physicochemical characterization of V2 O5-WO3/TiO2 De-NOx catalysts[J]. Journal of Catalysis, 1995, 155(1): 117-130.[11] Gheorghe C, Gee B. Solid-state vanadium-51 NMR studies of supported V2O5-WO3/TiO2 catalysts[J]. Chemistry of Materials, 2000, 12(3): 682-685.[12] Tang F, Xu B, Shi H, et al. The poisoning effect of Na+ and Ca2+ ions doped on the V2O5/TiO2 catalysts for selective catalytic reduction of NO by NH3[J]. Applied Catalysis B Environmental, 2010, 94(1-2): 71-76.[13] Tang F S. Effect of dispersion state and surface properties of supported vanadia on the activity of V2O5/TiO2 Catalysts for the Selective Catalytic Reduction of NO by NH3[J]. Chinese Journal of Catalysis, 2012, 33(4-6): 933-940.[14] Amiridis M D, Duevel R V, Wachs I E. The effect of metal oxide additives on the activity of V2O5/TiO2 catalysts for the selective catalytic reduction of nitric oxide by ammonia[J]. Applied Catalysis B Environmental, 1999, 20(2): 111-122.[15] 杨立娟, 李晓伟, 刘斌, et al. MO(M=Cu和Ni)/TiO2/γ-Al2O3催化剂在CO+O2反应中的活性[J]. 无机化学学报, 2007, 23(10): 1717-1722.[16] 陈铜. 氧化镍中非化学计量氧在乙烷氧化脱氢中的作用[J]. 催化学报, 1998, 19(1): 37-41.[17] Bao Z, Li W, Xu H, et al. Correlation between the characteristics and catalytic performance of Ni-V-O catalysts in oxidative dehydrogenation of propane[J]. Catalysis Letters, 2004, 94(1): 125-129.[18] Cheng K, Liu J, Zhang T, et al. Effect of Ce doping of TiO2 support on NH3-SCR activity over V2O5-WO3/CeO2-TiO2 catalyst[J]. Journal of Environmental Sciences, 2014, 26(10): 2106-2113.[19] Larrubia M A, Busca G. An ultraviolet-visible-near infrared study of the electronic structure of oxide-supported vanadia-tungsta and vanadia-molybdena[J]. Materials Chemistry & Physics, 2001, 72(3): 337-346.[20] Zhang S, Zhong Q. Surface characterization studies on the interaction of V2O5-WO3/TiO2 catalyst for low temperature SCR of NO with NH3[J]. Journal of Solid State Chemistry, 2015, 221: 49-56.[21] Wang D, Tang J, Zou Z, et al. Photophysical and photocatalytic properties of a new series of visible-light-driven photocatalysts M3V2O8 (M = Mg, Ni, Zn)[J]. Cheminform, 2012, 36(50): 5177-5182.[22] 徐爱菊, 照日格图, 贾美林, 等. Ni3V2O8催化性能与X射线光电子能谱分析[J]. 光谱学与光谱分析, 2007,27(10): 2134-2138.[23] Went G T, Li J L, Lombardo S J, et al. Raman spectroscopy and thermal desorption of ammonia adsorbed on titania (anatase)-supported vanadia[J]. Journal of Physical Chemistry, 1992, 96(5): 2235-2241.