Abstract：Ti（C0.7N0.3）-based cermets were prepared by low pressure sintering of powder metallurgy method. The effect of Co/（Co＋Ni） ratio on microstructure and mechanical properties were investigated using SEM， EDS and mechanical properties test instrument. Results show that after sintering at 1 400 ℃ for 1 h， the microstructure of Ti（C0.7N0.3）-based cermets is composed of black core， grey shell and white binder phase. When the total binder is 20% （mass percent） and Co/（Co＋Ni） ratio increases from 0 to 0.6， the bending strength of the cermet gradually increases to the maximum of 2 210 MPa， and then decreases gradually； while the hardness of the cermet reaches the maximum value of 92.1 HRA and then tends to be stable and no longer changes significantly with the increase of Co/（Co＋Ni） ratio.
李 朝，李 楠，柳学全，蔺 菲，李发长. Co和Ni对Ti（C0.7N0.3）基金属陶瓷组织和力学性能的影响[J]. , 2019, 29(01): 37-41.
LI Chao，LI Nan，LIU Xue-quan，LIN Fei，LI Fa-chang. Effect of binder Co and Ni on the microstructure and mechanical properties of Ti（C0.7N0.3）-based cermets. , 2019, 29(01): 37-41.
[1] RAJABIA,GHAZALIMJ,DAUDAR.Chemical composition,microstructure and sintering temperature modifications on mechanical properties of TiC-based cermet: a review[J].Materials&Design,2015,67:95-106.[2] XUQZ,AIX,ZHAO J,et al. Effect of heating rate on the mechanical properties and microstructure of Ti(C,N)-based cermets[J]. Materials Science and Engineering: A,2015,628:281-287.[3] 羊建高，谭敦强，陈颢. 硬质合金. 长沙：中南大学出版社[M]，2012：271-273.[4] 吴鹏. Ti(C,N)基金属陶瓷的强韧化及梯度结构制备技术的研究[D]. 南京：南京航空航天大学，2014.[5] 南晴.高强韧耐腐蚀Ti(C,N)基金属陶瓷的研究[D]. 长沙：中南大学粉末冶金研究院，2013.[6] A.Rajabi,M.J.Ghazali,J.Syarif,A.R.Daud.Development and application of tool wear:A review of the characterization of TiC-based cermets with different binders[J].Chemical Engineering Journal,2014,225:445-451.[7] D.I.Chun,D.Y.Kim,K.Y.Eun.Microstructural Evolution during the Sintering of TiC-Mo-Ni Cermets [J].Journal of the American Ceramic Society,1993,76(8):2049-2052.[8] 周书助. 超细Ti(CN)基金属陶瓷粉末成形性能及刀具材料的研究[D]. 长沙：中南大学，2006.[9] 瞿峻. Ti(CN)基金属陶瓷增强技术及组织和性能研究[D]. 武汉：华中科技大学，2010.[10] Vinod K. Sarin?.Comprehensive Hard Materials. 长沙：Elsevier Ltd [M].2014：160-165.[11] 张大勇，石增敏. 原始成分组成对 Ti(C,N)基金属陶瓷烧结性能的影响[J]. 粉末冶金技术，2013,30(2)：83-89.[12] Z.Shi，D.Zhang，S.Chen，T.Wang.Effect of nitrogen content on microstructures and mechanical properties of Ti(C,N)-based cermets [J]. Journal of Alloys and Compounds,2013,568:68-72.[13] N.Liu，S.Chao，X.Huang.Effects of TiC/TiN addition on the microstructures and mechanical properties ofultra-fine grade Ti(C,N)-Ni cermets [J].Journal of the European Ceramic Society,2006,26(16):3861-3870.[14] Q.Yang，W.Xiong，S.Li，J.Li. Effect of partial substitution of Cr for Ni on densification behavior,microstructure evolution and mechanical properties of Ti(C,N)-Ni-based cermets [J].Journal of Alloys and Compounds,2011,509(14）：4828-4834.[15] 黄培云. 粉末冶金原理. 北京：冶金工业出版社[M], 2015:307-314.[16] Vinod K. Sarin .Comprehensive Hard Materials. Elsevier Ltd [M].2014：207.[17] Ahn, S. Y., & Kang, S. Formation of core/rim structures in Ti(C, N)-WC-Ni cermets via a dissolution and precipitation process. Journal of the American Ceramic Society[J]. 2000，83：1489–1494.[18] Vinod K. Sarin .Comprehensive Hard Materials. Elsevier Ltd [M].2014：275-290.[19] P.Ettmayer，H.Kolaska，W.Lengauer. Ti(C,N) Cermets-Metallurgy and Properties[J]. Refractory Metals&Hard Materials.1995，13：343-351.[20] Vinod K. Sarin?.Comprehensive Hard Materials [M].2014：175.
2019, Vol. 29 