Wear Resistance of WC-12Co Coating Prepared by High Velocity Oxygen Fuel Spraying
WU Xu1, GUO Zhi-meng1, YU Ji-ping2
1. School of Materials Science and Engineering, University of Science Technology Beijing, Beijing 100083, China 2. AVIC Xi’an Aero-Engine Group Limited Company, Xi’an 710021, China
Abstract:WC-12Co coating was prepared by high velocity oxygen fuel (HVOF) spraying technology. The coating porosity, micro-hardness and the bonding strength between the substrate and coating were measured by IA32 quantitative analysis software, LM700AT automatic micro-hardness tester and universal testing machine, respectively. In addition, the tribological properties of the coating were tested on MRH-3 high-speed ring-on-block machines. The results show that the coating porosity is 0.33%, the micro-hardness is 1 393 HV, and the coating adhesive strength is higher than 64.4 MPa. With the test load of 800 N, the rotate speed of 1 000 r/min, the friction pair of GCr15, the experimental period of 1 h and the Great Wall CJ-4 15W/40 as lubricating oil, the friction coefficient of the coating remains at 0.099, the weight loss of the coating is 0.001 6 g. The wear mechanism is abrasive wear.
Sidhu.T.S,Prakash[J].S, and Agrawal. R.D. Studies on the properties of high-velocity oxy-fuel thermal spray coatings for higher temperature applications [ J ] . Materials Science, 2005, 41(6):805-823
Li H, etal.Young’s modulus and fracture toughness determination of high velocity oxy-fuel-sprayed bioceramic coatings [J].[J].Surf Coat Techn,, 2002, , 155:21-25
YANG Q, SENDA T, OHMORI A.Effect of carbide grain size on microstructure and sliding wear behavior of HVOF-sprayed WC-12Co coatings[J].Wear, 2003, 254(12):23-34