添加Cu粉对GCr15磨屑粉体性能的影响

doi:10.13228/j.boyuan.issn1006-6543.20140047

Abstract
Figure/Table
References
Related Citation (3)

Download: PDF (0 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract The compaction law of GCr15 bearing steel powder was analyzed. Influences of Cu addition on the green density, spring-back, sintered density and performance were explored, and the effect of pressure and sintering temperature on the density and hardness was studied. The results show that the compaction law of GCr15 bearing steel powder is accorded with Huang Pei-yun compaction equation. The green density increases with increasing pressure lower than 1 300 MPa, and the sintered density increases with increasing sintering temperature lower than 1 300 ℃. Addition of copper can improve the green and sintered density, but has little effect on the spring-back. For the GCr15 compacts without copper, the green density of 6.60 g/cm3 and spring-back of 1.73% are obtained when the pressure is 1 200 MPa, and after sintered at 1 150 ℃ for 2 h in H2 atmosphere, the sintered density is 6.91 g/cm3. While the compacts of GCr15 bearing steel powders with 5% (mass percent) copper powder sintered at 1 300 ℃ for the same time and in the same atmosphere, the density of 7.23 g/cm3 and the hardness of 36.3 HRC are achieved.

Key words： GCr15 bearing steel Density Spring-back Copper powder Hardness

Received: 20 May 2014 Published: 28 February 2015

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHONG Hong-Hai
	SHEN Wen-Hao
	DAN Na
	YU Ya-Lan
	NI Di
	JIANG Yang

Cite this article:

ZHONG Hong-Hai,SHEN Wen-Hao,DAN Na, et al. Effect of adding copper powder on the properties of GCr15 powder from grinding chips[J]. , 2015, 25(01): 32-37.

URL:

http://edit.chinamet.cn/Jweb_fmyjgy/EN/10.13228/j.boyuan.issn1006-6543.20140047 OR http://edit.chinamet.cn/Jweb_fmyjgy/EN/Y2015/V25/I01/32

[1]	曾德麟．.粉末冶金材料[M]．北京：冶金工业出版社，1997．19~38．
[2]	刘传习，周作平，解子章，等．粉末冶金工艺学[M] ．北京：科学普及出版社，1985．223~299．
[3]	张华诚．粉末冶金实用工艺学[M]．北京：冶金工业出版社，2004．27~102．.
[4]	周作平，申小平．粉末冶金机械零件实用技术[M]．北京：化学工业出版社，2006．302~324．
[5]	杨建东，田春林，金海峰，等．. 固着磨料研磨对工件表面残余应力的影响[J]．[J].中国表面工程, 2002, (（4）):37-38
[6]	米谷茂．残余应力的发生与对策[M]．朱荆璞，邵会孟，译．北京：机械工业出版社，1983：152．
[7]	戴伟.钢球化退火工艺设计[J].武汉理工大学学报, 2002, 26(1):138-140
[8]	马宝国，杨洪波，朱伏先，等.轴承钢中渗碳体的奥氏体化行为研究[J].热加工工艺, 2009, 38(20):5-10
[9]	闫文凯，杨卯生，杜景红，等.高纯净轴承钢组织演变与快速球化工艺的研究[J].钢铁, 2010, 45(12):63-67
[10]	谢学智.强韧化研究[J].金属热处理, 1984, 38(4):35-38
[11]	赵克达，朱世根，丁浩.细薄件的回火工艺研究[J].热加工工艺, 2013, 42(14):153-156
[12]	李元元，李金花，倪东惠.润滑剂含量对模壁润滑温压工艺的影响[J].粉末冶金技术, 2004, 22(6):341-344
[13]	陈进，肖志瑜，李超杰，等.铁粉的高速冲击复压成型[J].粉末冶金工业, 2010, 20(6):18-21
[14]	黄培云．粉末冶金原理（第二版）[M]．北京：冶金工业出版社，1997．183~195．
[15]	蒋阳，许煜汾.含成形剂的纳米微晶粉末压形规律的研究[J].无机材料学报, 1999, 14(1):165-169
[16]	王维华，蒋阳，仲洪海.自燃法合成粉末及其热电性能[J].硅酸盐学报, 2007, 35(10):1282-1286
[17]	张海青，仲洪海，管其刚，等.自蔓延法制备.-+δ粉体及其性能研究[J].粉末冶金工业, 2010, 20(6):36-40
[18]	仲洪海，王文龙，张海青，等.用甘氨酸法合成.粉体及热电性能表征[J].粉末冶金材料科学与工程, 2011, 16(1):32-37
[19]	徐润泽．粉末冶金结构材料学[M]．长沙：中南工业大学出版社，2002．21~47．
[20]	BEISS.P. Effects of density on properties,conductivity and machinability of stainless steel[J].Metal Powder Report, 1998, 53(6):39-42