| Microstructure and performance of WC-12Co coating prepared by APS |
| LIU An-qiang1,2,ZHU Hong-bin1,2,YUAN Jian-peng1,2,HOU Wei-ao1,2 |
（1. Beijing General Research Institute of Mining & Metallurgy, Beijing 100160, China
2. Beijing Engineering Research Center on Surface Strengthen and Restoration of Industrial Parts, Beijing 102206, China） |
|
|
|
|
Abstract WC-12Co coating was deposited on steel 45 by atmospheric plasma spraying (APS) process. The microstructure and phase composition of the coating were analyzed by SEM and XRD, respectively; microhardness tester and universal tester were used to measure the microhardness and bonding strength of the coating, respectively; the friction and wear resistance of the coating were examined using SRV-Ⅳ friction wear tester. The results indicate that, the WC-12Co coating is dense and uniform, only a small amount of WC decomposes during spraying process and small amount of W2C and Co3W3C phases are observed in the coating. The coating exhibits high mechanical properties, the average bonding strength is 50.63 MPa, the surface micro-hardness of the coating is 85.7 HR15N, and the micro-hardness of cross section is 1 053.8 HV0.3, respectively. Compared with the 304 stainless steel, WC-12Co coating exhibits excellent wear resistance. Abrasive wear is the major wear mechanism for the coating from room temperature to 300 ℃.
|
|
Received: 20 May 2015
Published: 08 December 2015
|
|
|
|
| [1]Stewart D A, Shipway P H, Mccartney D G.Microstructural evolution in thermally sprayed WC-Co coatings: comparison between nanocomposite and conventional starting powders[J].Acta Materialia, 2000, 48(7):1593-1604
[2] Yang Q, Senda T, Hirose A.Sliding wear behavior of Wc-12%Co coatings at elevated temperatures.[J].Suface & Coating Technology, 2006, 200(5):4208-4212
[3]丁彰雄, 陈伟, 王群, 等.制备的多峰- 涂层摩擦磨损特性[J].摩擦学学报, 2011, 31(5):425-430
[4] 李博宇.等离子喷涂纳米结构WC-12Co涂层的制备与性能[D]. 大连：大连理工硕士论文，2006.
[5] 周庆发.等离子喷涂技术[M]. 南京：江苏科学技术出版社，1982.
|
|
|
|
2015, Vol. 25 