Effect of Heat treatment Process on Microstructure and Properties of Tool steel 75Cr1
摘要 本文以Nb微合金化的75Cr1钢为基础，分析了Nb元素添加后75Cr1钢在热处理过程中组织和性能的变化规律，研究了Nb元素在钢中的析出行为。结果表明，Nb元素的添加能够提高钢的性能稳定性和屈强比，并且显著地提高钢的低温冲击韧性。
关键词 ：
Nb合金化 ,
工具钢 ,
热处理 ,
强化 ,
韧性
Abstract ：In this paper, about 0.02 wt.% Nb element was added to the tool steel 75Cr1, the microstructure and property of 75Cr1 during heat treatment was analyzed, and the precipitation behavior of Nb element was studied. The results show that, the adding of 0.02 wt.% Nb can effectively improve the property stability and yield ratio of steel, and the impact toughness of steel at low temperature is also improved obviously.
Key words ：
Nb alloying
Tool steel
Heat Treatment
Strengthen
Toughness
收稿日期: 2020-04-30
出版日期: 2020-12-22
通讯作者:
雍兮
E-mail: yongxi@nercast.com
[1]曾斌, 李昭东, 孙新军, 杨俊伟, 雍岐龙.新型锯片基体用钢的研究与开发[J].钢铁, 2016, 51(02):78-83
[2] 李定乾.金刚石圆锯片基体的选材及预应力调整[J].金刚石与磨料磨具工程, 1997, 99(3):37-39
[3] 齐俊杰, 黄运华, 张跃.微合金化钢[J].冶金工业出版社, 2006, :-
[4] L.Meyer.History of Niobium As a Microalloying Element[J].Niobium-science & Technology (TMS), 2001, ( ): -
[5]刘宗昌，计云萍.热处理原理中概念的更新[J].热处理技术与装备, 2019, 40(03):1-5
[6] 雍岐龙.钢铁材料中的第二相[J].冶金工业出版社, 2006, :-
[7]巫宇峰, 惠卫军, 陈思联, 等.钒对中碳非调质钢组织性能的影响[J].钢铁研究学报, 2016, 28(11):56-62
[1]
李小平 张亚军. 超导复合线用小规格Nb47Ti棒材加工工艺研究
[2]
严飞 于一鹏. 低膨胀合金磁特性及其温度稳定性研究
[3]
陈明昕 杨晓江. Nb元素添加对75Cr1相变的影响
[4]
雷国财. HVAF喷涂WC-12Co涂层的应用研究
[5]
李勃 王帅. 热处理工艺对3Cr13MoCu不锈钢组织及性能的影响
[6]
赵润飞 祖方遒. 熔体过热处理对P型(Bi,Sb)2(Te,Se)3合金凝固行为、组织及电学性能的影响
[7]
魏媛，李玉卿，张东涛，岳明. SmCo5非晶磁体的磁场热处理研究
[8]
吕耀辉，王凯博，刘玉欣，林建军 ，徐滨士. 热处理对等离子弧增材制造Inconel 718合金组织与性能的影响
[9]
曹迪 王宇鑫 高伟东 金云学. 铍青铜材料的加工工艺研究进展
[10]
王立涛 施立发 朱国辉 夏雪兰. 硅钢热处理过程涂层中铬的转化试验研究
[11]
王维斯 吴强. T92与Super304H异种钢焊接接头硬度异常分析及处理
[12]
吴仡璇，罗强，焦津，沈军. 热处理对Fe基非晶涂层结构与性能的影响
[13]
张伟，刘天成，朱景森，李德仁，卢志超. 退火热处理对扁平状Fe- Si- Al磁粉电磁性能的影响
[14]
郭晓凡，寇生中，蒲永亮，曲红霞，董天文，张志栋. 熔体过热处理工艺对GH4169合金组织和力学性能的影响
[15]
生利英. 热处理对Gd3Al2-xGax系合金磁热效应的影响
2020, Vol. 27 