Abstract In order to achieve high-quality brazing connection of high-temperature titanium alloy Ti65, three components of Ti-based amorphous brazing filler with Zr as the variable were prepared using vacuum rapid quenching technology, and Ti65 was brazed according to the optimal welding process of the three brazing filler. The microstructure and element distribution characteristics of three types of brazing joints were analyzed using scanning electron microscopy, and the tensile properties of the joints at room temperature and 650 ℃ were compared and analyzed. The experimental results show that the three types of brazing filler have good surface quality and no pores, and can achieve Ti65 brazing connection. The joint is mainly composed of layered Widmannstatten structure, but there is a continuous compound phase in Ti-13Zr-Cu-Ni brazing filler. The mechanical performance results show that the room temperature and 650 ℃ high temperature tensile properties of the three brazing filler can reach over 90% of the tensile strength of the base material. The room temperature tensile strength of Ti-13Zr -Cu-Ni brazing material is slightly lower, and the fracture mainly occurs at the joint interface, exhibiting brittle fracture. The fracture of the Ti-Cu-Ni brazing material room temperature and 650 ℃ high temperature tensile sample occurs at the base material, showing mechanical properties equivalent to the matrix.
|
Received: 09 October 2023
Published: 22 February 2024
|
|
|
|
1. 李文渊, 刘建荣, 陈志勇等. Ti60合金板材的室温强度与其显微组织和织构的关系[J]. 材料研究学报, 2018, 32(6): 455.2.Liu Z, Liu P, Wang L, et al. Fatigue properties of Ti-6.5Al-3.5Mo-l.5Zr-0.3Si alloy produced by direct laser deposition [J]. Mat. Sci.Eng. A, 2018, 716: 140.3.王清江, 刘建荣, 杨 锐. 高温钛合金的现状与前景[J]. 航空材料学报, 2014, 34(4): 1.4. 毛小南, 赵永庆, 杨冠军. 国外航空发动机用钛合金的发展现状 [J]. 中国材料进展, 2007, 26(5): 1.5. Davies P, Pederson R, Coleman M et al. The hierarchy of micro-structure parameters affecting the tensile ductility in centrifugally cast and forged Ti-834 alloy during high temperature exposure in air [J]. Acta Mater., 2016, 117: 51.6. 王国强, 赵子博, 于冰冰等. 热处理工艺对Ti6246钛合金组织与力学性能的影响[J]. 材料研究学报, 2017, 31(5): 352.7. 吴汐玥, 陈志勇, 程超, 刘建荣等. 热处理对Ti65钛合金板材的显微组织、织构及拉伸性能的影响[J]. 材料研究学报, 2019, 33(10): 785.8. 岳颗. Ti65合金显微组织及关键高温力学性能研究[D];中国科学技术大学,2019.9. 李文渊.Ti60髙温钛合金板材织构与力学性能各向异性研究[D];中国科学院金属研究所,2018.10. 赵永庆,洪权,葛鹏.钛及钛合金金相图谱[M].中南大学出版社, 2011. |
|
|
|