Abstract:LiNi0.5Co0.2Mn0.3O2, the eligible ternary cathode materials of lithium ion batteries, were synthesized by sol-gel self propagating combustion method using waste NiCoMn ternary material as raw material. The composite was characterized by TG, XRD, SEM and land testing. The results indicate that the material not only has a good layered structure, but also has porous properties. The discharge capacity of the product synthesized at pH=8 is 164.6 (mA·h)/g in 2.75-4.30 V at 0.2 C, the coulomb efficiency is about 85.8%, and the capacity retention rate is about 94.9% after 30 cycles. This material is an excellent ternary cathode material with high discharge specific capacity.
李伟伟. pH值对溶胶-凝胶自蔓延燃烧法制备LiNi0.5Co0.2Mn0.3O2的影响研究[J]. , 2018, 28(06): 38-41.
LI Wei-wei. Effect of pH value on the preparation of LiNi0.5Co0.2Mn0.3O2 by sol-gel self-propagating combustion method. , 2018, 28(06): 38-41.