Abstract:During the recycling process of sintered Nd-Fe-B magnets, rare earth elements will be oxidized and lost, thus the densification of the recycled magnets is interfered. The addition of Ce metal is helpful to densify the recycled magnet and optimize the microstructure of the magnet. Through the addition of low-cost Ce metal, the comprehensive performance of the recycled magnet was successfully optimized. The hydrogen absorption process of waste sintered Nd-Fe-B magnets was also studied. The magnetic properties of the recycled magnets were tested by BH tester, and the microstructure of the magnet was observed by scanning electron microscopy. The results show that when 4% Ce ( mass percent ) is added, the remanence of the recycled magnet reaches more than 98% of that of the original magnet, and the intrinsic coercivity exceeds that of the original magnet under the conditions of 1 350 K sintering and 773 K heat treatment.
梅莉萍. 废旧烧结Nd-Fe-B磁体添加Ce再制造技术研究[J]. , 2018, 28(04): 77-81.
MEI Li-ping. Study on the remanufacturing technology for sintered Nd-Fe-B magnets bulk wastes adding Ce. , 2018, 28(04): 77-81.
[1]张雪峰,王大鹏,张倩.钕铁硼废料回收利用[[J].科技创新导报,2012(13):149-150.[2]李超.废旧稀上钕铁硼永磁材料的回收与再利用研究[D].北京工业大学,硕士,2014:40-50[3] M. Zakotnik, I. R. Harris, A. J.Williams. Multiple recycling of NdFeB-type sintered magnets[J]. Alloys Compd, 2009,469: 314-321.[4}李超,刘卫强,张东涛,岳明,张久兴.NdH纳米助剂回收制备烧结钱铁硼永磁体的研[J].功能材料.2014, 17(45):17059-17061.[5]李现涛 ,岳明,等. 块状烧结钕铁硼废料的氢处理回收技术研究进展.稀土. 2016. 39(3): 123-128. [6]李现涛. 烧结钕铁硼废料的再制造技术及机理研究[D].北京工业大学,博士2016:54-56.[7 ]张月明 Ce磁体的力学性能及Ce对再生磁体微结构的影响[D].钢铁研究总院,硕士2017:59-72.[8]周寿增,董清飞.超强永磁体一一稀土铁系永磁材料[M].北京:冶金工业出版社,1999[9] M. Zakotnik, E. Devlin, I. R. Harris, A. J. Williams. Hydrogen Decrepitation and Recycling of NdFeB-type Sintered Magnets[C]. Proceedings of 19th International Workshop on Rare Earth Permanent Magnets&Their Applications, 2006: 289-295.[10]周寿增,董清飞,高学绪.烧结钕铁硼一一稀土永磁材料与技术[M].北京:冶金工业出版社,2011.[11]黄书林.含Ce磁体微结构与磁性能的研究[D]. 2015.[12]张月明 Ce磁体的力学性能及Ce对再生磁体微结构的影响[D].钢铁研究总院,硕士2017:66-68.