Abstract:Cobalt was recovered from the low acidic leaching residue of spent lion batteries by sulfating roasting-leaching process. X-ray diffraction shows that Co3O4 is the main phase of raw materials that is difficult to leach. The results show that nearly 99.86% of cobalt is leached out under optimal conditions, the roasting temperature is 350 ℃, H2SO4-to-raw material mass ratio is 0.8, and roasting time is 1 h.
周荣超,鲁俊雀,叶民杰,王榆彬,王 杜. 低酸富钴渣硫酸化焙烧及浸出[J]. 粉末冶金工业, 2020, 30(02): 90-88.
ZHOU Rong-chao, LU Jun-que, YE Min-jie, WANG Yu-bin, WANG Du. Cobalt enriched wlag from the low acidic leaching of spent li-ion batteries by sulfuting roasting and leaching. Powder Metallurgy Industry, 2020, 30(02): 90-88.