Abstract:TiAl alloy targets were prepared by pressureless sintering and hot pressing sintering respectively, and TiAl hard coatings were prepared by sputtering deposition method. The microstructure and phase composition of the hard coatings were analyzed, and the high temperature oxidation resistance and mechanical properties of the coatings were also tested. The results show that the hard coating of target material prepared by pressureless sintering is poor in compactness, uneven in dispersion, fast in oxidation rate and only 1 798 HV in microhardness. While the hard coating of target material prepared by hot pressing sintering has the advantages of high density, low porosity, fine grain size, uniform distribution, significantly improved oxidation resistance, which microhardness is as high as 3 165 HV, 76% higher than the former.
收稿日期: 2017-12-19
出版日期: 2018-08-29
基金资助:广东省高职教育品牌专业建设项目成果
通讯作者:
戴护民
E-mail: 104666515@qq.com
引用本文:
戴护民,许巨忠. TiAl镀膜靶材制备工艺对硬质涂层的性能影响研究[J]. , 2018, 28(04): 17-20.
DAI Hu-min,XU Ju-zhong. Effect of TiAl target preparation process on properties of hard coatings. , 2018, 28(04): 17-20.
[1]梁俊才,穆健刚,张凤戈,等.硬质涂层用镀膜靶材的研究[J].粉末冶金工业,2014(24):38-43.[2]王赛玉,蔺绍江,陈肖.TiAlCrN涂层高温氧化行为[J].中国有色金属学报,2013(23):2267-2272.[3]陈希,黄蓉,邬晔.钛铝合金溅射镀膜靶材的研究进展[J].湖南有色金属,2012(28):51-53.[4]KIMURA A,HASEGAWA H,YAMADA K, et al. Effects of Al content on hardness,lattice parameter and microstructure of Ti1-x Alx N films[J]. Surf Coat Tech, 1999, 120:438-441.[5]陈 利.Ti-Al-N 基硬质涂层的热稳定性能/微结构及其力学/切削性能的研究[D].长沙:中南大学,2009:67.[6]童洪辉.物理气相沉积硬质涂层技术进展[J].金属热处理,2008,33(1):91-93.[7] 张进.35CrMo钢表面化学气相沉积多层硬质涂层的结构与性能研究[J].真空科学与技术学报,2013,33(7):715-720.[8]杜日昇.高Al含量Ti-Al-N系硬质涂层的制备及其抗氧化性能的研究[D].广东,华南理工大学,2011.[9] Barshilia H. C, Acharya S, Ghosh M, et al. Performance evaluation of Ti Al Cr YN nano- composite coatings deposited using four-cathode reactive unbalanced pulsed direct current magnetron sputtering system[J]. Vacuum 85(2010):411-420.