Abstract:In this paper,oil drilling cuttings were taken as main raw material,appropriate conditioner was added,
and sintered to produce porous ceramic filter material. Under the condition of holding time of 60 min,and the content
of coagulant is 5%,the pore-forming agent is 10%,the reinforcing agent is 12%,the sintering temperature is
1 050 ℃,the porosity of the porous ceramic material is 24.43% to 57.11%,and alkali resistance is 99.96%,the
acid resistance is 92.22%. The color,corrosion and heavy metal content of the leaching solution all meet the national
standards;with Cr(Ⅵ)as the adsorption object,preparing simulated wastewater containing Cr,and investigating
the adsorption performance of porous ceramics as an adsorbent. Under the condition of absorbing time is
300 min,and the pH of the solution is 5,the addition amount of the ceramic material is 60 g/L,the initial concentration
of Cr is 80 mg/L,the maximum adsorption efficiency of porous ceramics can be achieved. In this paper,
the environmental friendly products were prepared and the waste resources were utilized.
张太亮,唐闻一,钟继超,袁磊. 含油钻屑制备多孔陶瓷及其吸附性能[J]. 粉末冶金工业, 2020, 30(05): 29-33.
ZHANG Tai-liang,TANGWen-yi,ZHONG Ji-chao,YUAN Lei. Study on preparation of porous ceramic material by oil-containing cuttings and
it’s adsorption properties. Powder Metallurgy Industry, 2020, 30(05): 29-33.