Abstract:In this study, the surface modification treatment of FeSiCr alloy powder was carried out with zinc-man‐
ganese phosphating solution. Vibrating sample magnetometer, impedance analyzer and soft magnetic material AC
test device were used to analyze effects of the content of zinc-manganese phosphating solution on saturation mag‐
netization of FeSiCr magnetic powder, effective permeability and power loss of FeSiCr magnetic powder cores.
The results show that with the increase of the concentration of zinc-manganese phosphating solution, the saturation
magnetization of the composite magnetic powder core gradually decreases, the power loss first decreases and then
increases. When the concentration of zinc-manganese phosphating solution is 25%, the effective permeability is
39.5, and the power loss is only 103.6 W·kg-1 (100 kHz, 50 mT).
收稿日期: 2022-11-02
作者简介: 何正烨(1998—),男,硕士,主要研究方向为金属软磁复合材料制备及性能。
引用本文:
何正烨,罗 剑,安 静,徐立红,牟 星,郭世海. 磷化工艺对FeSiCr软磁复合材料磁性能的影响[J]. 粉末冶金工业, 2024, 34(02): 86-90.
HE Zhengye,LUO Jian,AN Jing,XU Lihong,MU Xing,GUO Shihai. Influence of phosphating process on magnetic properties of FeSiCr soft magnetic composites. Powder Metallurgy Industry, 2024, 34(02): 86-90.