Abstract：With fine tungsten powder, electrolytic nickel powder and carbonyl iron powder as raw material, the oversized parts 97W2Ni1Fe alloy was prepared by liquid phase sintering. The weight of 97W2Ni1Fe oversized parts was 66 kg and the size was [?]120 mm×320 mm. The oversized part was cut into 52 parts, and then densities and microstructure of the 52 parts were measured and analyzed, respectively, to study the density and microstructure uniformity. Results show that the density and microstructure of the oversized tungsten alloy have regular distribution. Because of time effect of heat conduction during sintering, the density and tungsten particle size both decrease gradually from surface to the interior of the workpieces.
王 玲，刘桂荣，裴燕斌. 97WNiFe合金超大制件的密度和显微组织均匀性研究[J]. , 2015, 25(05): 56-59.
WANG Ling, LIU Gui-rong, PEI Yan-bin. Study on density and microstructure uniformity of 97WNiFe oversized parts. , 2015, 25(05): 56-59.
[1]王伏生，赵慕岳，梁荣海，周载明．WNiCu合金材质均匀性的工艺因素研究[J]．粉末冶金技术，1993,11(1):37-42．[2]刘桂荣，蒲治军，王玲，裴燕斌．细晶钨合金密度均匀性研究[J]．粉末冶金工业，2010,4:24-27．[3] German R M. Liquid Phase Sintering，Plenum Press，NY，1985，12[4]邓欣，周国安. W-Ni-Fe 高比重合金烧结机理、显微组织及对力学性能的影响[J]. 中国钨业，1997（4）：18-24.[5] German R M et al. Metall. Trans A，1984，15A：747-754.
2015, Vol. 25 