Abstract：As a permanent magnet material with high magnetic energy product， bonded NdFeB magnets have been widely used in aerospace， nuclear industry， transportation and other fields. Its raw material is NdFeB rapid quenching powder. The NdFeB magnets are easy to corrode in air environment， in order to ensure the reliability and life of bonded NdFeB magnets， the corrosion behavior of magnets with corrosion defect after protective treatment was studied. It is found that the corrosion grows continually and the magnetic performance decreases even though the magnet has reliable coating protection. The corrosion rates of magnets with different damage degrees are different. With the increase of corrosion time， the previous corrosion product Fe2O3 reacts with water to produce H2， accelerating the corrosion of damaged magnets.
[1]Tenaud P, Vial F, Sagawa M.Improved corrosion and temperature behavior of modified NdFeB magnets[J].IEEE Trans Magn, 1990, 26(5):1930-1932[2]李广宇，孟瑶等.水溶性缓蚀剂对钕铁硼永磁材料的防腐蚀性能[J].材料保护, 2009, 42(12):49-51[3]王恩生.钕铁硼化学转化膜防腐蚀技术[J].电镀与精饰, 2013, 35(12):13-17[4]祝景汉.快淬钕铁硼永磁合金及粘结磁体[J].粉末冶金工业, 2000, 10(1):40-45[5]周维娜等.快淬粘结磁体制备工艺及其对磁性能的影响[J].金属功能材料, 2005, 6(12):28-32[6] Bala H，Trepak N M.Corrosion protection of NdFeB type permanent magnets by zinc phosphate surface conversion coatings[J]. Intermetallics, 2001, (9):515-519.[J].Intermetallics, 2001, (9):515-519[7]Bernardi J, Fidler J.Microstructural analysis of strip cast Nd-Fe-B alloys for high (BH)max magnets[J].J.Appl. Phys., 1998, 83(11):6396-6396[8]Yoshio Kato.Thermal stability of sintered and bonded rare-earth magnets[J].Journal of Applied physics, 1999, 85(8):4868-4870[9] Tamborim Takeuchi S M.Cerium conversion layer for improving the corrosion resistance of phosphate NdFeB magnets[J]. Surface & Coatings Technology, 2006, 201:3670-3675.[J].Surface & Coatings Technology, 2006, 201:3670-3675[10]林河成.国内钕铁硼永磁材料的高速发展[J].金属材料研究, 1999, 25(2):15-22[11]Mottram R.S., Williams A.J., Harris I.R..Blending additions of cobalt to NdFeB milled powder to produce sintered magnets[J]. Journal of Magnetism and Magnetic Materials, 2000, 217:27-34.[J].Journal of Magnetism and Magnetic Materials, 2000, 217:27-34[12]Gao Jian-rong, Song Xiao-ping, Wang Xiao-tian.Effects of reduced hydrogen pressure on magnetic properties of HDDR-treated NdFeGaB alloy powders[J].Journal of Alloys and Compounds, 1998, 267(6):270-273
2018, Vol. 28 