Preparation of ultrafine W-Ag composite powders by sol-gel method |
ZHANG Fu-bin1, HU Yan-ling2, HU Ye-qi2, XU Long-shan2, HU Bai-xin3 |
1. School of Mechanical and Automotive Engineering, Xiamen University of Technology, Xiamen 361024, China 2. School of Materials Science and Engineering, Xiamen University of Technology, Xiamen 361024, China 3. School of Materials Science and Engineering, Hu’nan University, Changsha 410082, China |
|
|
Abstract W-20%Ag (mass percent) composite powders were prepared by sol-gel method with AgNO3 and (NH4)6H2W12O40·5H2O as raw materials and citric acid as a chelating reagent.The decomposition process of dry gel was checked by means of thermogravimetric analysis. The phase composition, particle size and morphology of the powders were studied by XRD and SEM. The results show that precursor powders undertake a series of decomposing and compound reactions during calcination and reduction. With the increasing of temperature, the phase composition, particle morphology, as well as particle size of the powder change apparently. The granularity of the W-20%Ag (mass percent) composite powders is about 200-400 nm.
|
Received: 05 August 2014
Published: 28 February 2015
|
|
|
|
[1] |
张福斌,胡业奇,许龙山,陈永鑫.钨银复合材料应用与研究进展[J].材料导报, 2014,28:26-30.
|
[2] |
Sale F R, Albisten J N.Production and sintering of Ag-W composites containing Ni[J].Modern Developments in Powder Met, 1988, 19: 75-89.
|
[3] |
吕大铭.我国的钨铜、钨银材料的应用与发展[J].中国钨业, 1999, 5(6):182-
|
[4] |
孟繁琦,高家诚,王勇,李锐.银钨触头材料的制备工艺及使用性能[J].材料导报,2006,20:321.
|
[5] |
Aslanoglu Z, Karakas Y, Ovecoglu M L, Ozkal B.Effects of nickel addition on properties of Ag-W electrical contact materials[J]. Powder Metall, 2001, 44:77.
|
[6] |
胡可文,陈文革.熔渗法Ag W(75)触头材料研究[J].电工材料,2009,3:13
|
[7] |
Qureshi A H, Azhar S M, Hussain N.The effect of cobalt addition on sintering and microstructural behaviour of silver-tungsten (Ag-W) composite [J]. Therm Anal Calorim,2010,99:203
|
[8] |
Costa F A, Silva A G P, Filho F A, Gomes U U.Solid state sintering of a W–25 wt% Ag powder prepared by high energy milling[J].Refractory Metals&Hard materials, 2008, 26:318
|
[9] |
Taghavi Porian Azar G, Rezaie H R, Razavizadeh H.Synthesis and consolidation of W-Cu composite powders with silver addition[J].Journal of Refractory Metals and Hard Materials, 2012, 31: 157-163.
|
[10] |
Costa F A, Silva A G P, Filho F A, Gomes U U, Vieira F A.Synthesis of a nanocrystalline composite W–25wt% Ag powder by high energy milling[J].Powder Techn, 2008, 188:30
|
[11] |
曾德麟,周红翠.用化学共沉淀法制备-复合粉[J].中南矿冶学院学报, 1991, 22(6):670-
|
[12] |
Taghavi Porian Azar G, Rezaie H R, Gohari B, Razavizadeh H.Synthesis and densification of W-Cu, W-Cu-Ag and W-Ag composite powders via a chemical precipitation method[J].Journal of Alloys and compounds, 2013, 574:432-436
|
[13] |
Sahoo P K, Kamal S S K, Singh A K, Sreedhar B, Durai L, Srivastava S K.Facile chemical synthesis of W-Ag and W-Cu nanocomposites at low temperature[J].Journal of Nanoscience and Nanotechnology,2011,11:2506-2513.
|
|
|
|