| Braking properties of Cu-Fe based powder metallurgy braking materials |
| WANG Xiao-yang1,2,RU Hong-qiang1 |
1. School of Materials & Metallurgy, Northeastern University, Shenyang 110004, China
2. Liaoning Province Key Laboratory of Advanced Material Preparation Processing, Shenyang University, Shenyang 110044, China |
|
|
|
|
Abstract Using the cast steel as brake disc and Cu-Fe based powder metallurgy materials as braking materials to form a friction pair, the influence of braking speed (60-380 km/h) and braking pressure (0.3-0.5 MPa) on friction?coefficient,?braking temperature,?braking length and braking?torque of braking material was studied by using MM-1000Ⅱfriction and wear testing machine. The wear and the surface microstructure of the braking materials after braking test were analyzed. The results show that the friction coefficients of braking materials decrease with the increasing of braking speed. The increases in the braking pressure lead to the decreased braking distances and increased braking temperature. The wear mechanism of Cu-Fe based braking materials is mainly due to the fatigue wear, abrasive wear and oxidation wear at different braking speeds.
|
|
Received: 09 March 2015
Published: 08 December 2015
|
|
|
|
|
|
|
2015, Vol. 25 