Research on rheology of feedstock for Ni- Al2O3 powder injection molding |
FU Jie1,SHANG Feng2,3,LI Hua-qiang2,QIAO Bin2,3,CAO Zhen-wei1,SUN Wei2 |
1. School of Mechanical and Electrical Engineering, China University of Mining and Technology, Xuzhou 221116, China 2. School of Mechanical Engineering, Huaihai Institute of Technology, Lianyungang 222005, China 3. Jiangsu Key Laboratory of Large Engineering Equipment Detection and Control, Xuzhou Institute of Technology, Xuzhou 221111, China |
|
|
Abstract Ni-Al2O3 feedstock with 55% (volume percent) powder loading and diverse content of Ni was prepared in mixing module of HAAKE PolyLab QC torque rheometer. The formulation of binder is 60%PW+35%LDPE+5%SA (mass percent). The viscosity of feedstock was measured at MLW-400 capillary rheometer at 130 ℃, 140 ℃, 150 ℃. The value of power law exponent and flow activation energy was calculated through curvefit and regress of MATLAB. The results show that content of Ni has little influence on power law exponent of feedstock, which indicates the formulation of binder is appropriate and feedstock is homogeneous. However, the sensitivity of feedstock for temperature increases with the Ni content increasing. The experimental results provide reference to preparation of Ni-Al2O3 composites using powder injection molding and laid foundation on research of Ni content on properties of Al2O3 ceramic.
|
Received: 21 April 2015
Published: 01 February 2016
|
|
|
|
[1]乔斌, 付广柱, 冯立超等.注射成形-%的两步脱脂工艺[J].有色金属工程, 2014, 4(2):32-34
[2]朱棉霞, 徐序, 李月明等.金属颗粒增韧氧化铝陶瓷研究现状[J].中国陶瓷, 2012, 48(12):10-13
[3]卢红宪,蒋明学.基金属陶瓷的研究现状及发展趋势[J].中国陶瓷工业, 2007, 14(4):30-32
[4]范景莲,刘勋,黄伯云等.纳米金属陶瓷粉末的热压[J].粉末冶金技术, 2005, 23(2):120-124
[5] 张敬强,荣守范,丰崇友.氧化铝陶瓷增韧的研究现状[J].铸造设备研究,2006(2):40-43.[J].铸造设备研究, 2006, (2):40-43
[6]曾金珍,慕玮,杨建等.颗粒形貌对注凝成型 陶瓷性能的影响[J].复合材料学报, 2014, 31(2):416-422
[7] 虞钢,虞和济.激光制造工艺力学[M].北京:国防工业出版社,2012.229-230.
[8] 杨策.激光近净成形Al2O3/SiC复相陶瓷材料的研究[D].大连:大连理工大学,2013. 7-8.
[9] 付广柱,注射成形制备Cu/Al2O3复合材料工艺研究[D].徐州:中国矿业大学,2014. 8-10.
[10]程远胜,罗守靖.复合材料伪半固态触变模锻成形[J].复合材料学报, 2009, 26(6):116-120
[11] 王鹏翔.伪半固态触变成形Al /Al2O3复合材料工艺基础研究[D].哈尔滨:哈尔滨工业大学,2006.11-12.
[12]Abolhasani H, Muhamad N.A new starch-based binder for metal injection molding[J].Journal of Materials Processing Technology, 2010, 210(6):961-968
[13]Liu Z Y, Loh N H, Tor S B, et al.Characterization of powder injection molding feedstock[J].Materials characterization, 2002, 49(4):313-320
[14] Hidalgo J, Jiménez-Morales A, Barriere T, et al.Capillary rheology studies of INVAR 36 feedstocks for powder injection moulding[J]. Powder Technology, 2015, 273: 1-7.[J].Powder Technology, 2015, 273:1-7
[15]Fayyaz A, Muhamad N, Sulong A B, et al.Micro-powder injection molding of cemented tungsten carbide: Feedstock preparation and properties[J]. Ceramics International, 2014.41(3):3605-3612.[J].Ceramics International, 2014, 41(3):3605-3612
[16] 蒋忠兵,李笃信,李昆等.氧化锆陶瓷注射成形的喂料流变性能研究[J]. 粉末冶金技术, 2009 (6): 418-421.[J].粉末冶金技术, 2009, (6):418-421
[17]李益民,李云平.金属注射成形原理与应用[M].长沙:中南大学出版社, 2004. 73.
[18]Chen X, Lam Y C, Wang Z Y, et al.Determination of phenomenological constants of shear-induced particle migration model[J].Computational materials science, 2004, 30(3):223-229
[19]Huang B Y, Liang S Q, Qu X H.The rheology of metal injection molding[J].Journal of Materials Processing Technology, 2003, 137(1):132-137
[20]Li Y M, Huang B Y, Qu X H.Viscosity and melt rheology of metal injection molding feedstocks[J].Powder Metallurgy, 1999, 42(1):86-90
|
|
|
|