Research status of friction and wear properties and mechanism of automotive cam materials |
WANG Rui1,WANG Lin-shan1,2,3,LIANG Xue-bing1,2,3,ZHANG Wang1,WANG Li-min1,2,3,ZHANG Shao-ming1 |
(1. General Research Institute for Nonferrous Metals, Beijing 100088, China 2. GRIPM Advanced Materials Co., Ltd., Beijing 101407, China 3. Beijing Hengyuantianqiao Powder Metallurgy Co., Ltd., Beijing 101407, China) |
|
|
Abstract The automobile camshaft controls the intake and exhaust valves of the engine. The common failure mode of the camshaft is cam wear. The wear resistance of the cam has an important influence on the service life of the camshaft. The friction and wear testing methods of cam materials were introduced, the research status of friction and wear properties of casting, forging and powder metallurgy cam materials and the influence of microstructure on their wear resistance were discussed, the friction and wear mechanism of cam materials were also summarized, and some suggestions on the research of cam wear mechanism were finally put forward.
|
Received: 02 March 2017
Published: 12 October 2018
|
|
|
|
[1]Nakada M.Trends in engine technology and tribology[J].Tribology International, 1994, 27(1):3-8
[2] 汽车构造.陈家瑞[M].北京:机械工业出版社,2000: 86-87.
[3]Bayrakceken H,Ucun I,Tasgetiren S.Fracture analysis of a camshaft made from nodular cast iron[J].Engineering Failure Analysis, 2006, 13(8):1240-1245
[4] 菅昭彻哉,罗明炎.烧结一体化凸轮轴的开发[J]. 汽车工艺与材料, 1986(1).[J].汽车工艺与材料, 1986, 1(1):19-23
[5]钱人一.凸轮轴制造工艺综述[J].上海汽车, 2005, 31(03):26-30
[6] 王玉梅.装配式凸轮轴滚花联接工艺及装配参数仿真分析[D].吉林: 吉林大学,2015.
[7]Booth J E, Harvey T J, Wood R J K, et al.Scuffing detection of TU3 cam–follower contacts by electrostatic charge condition monitoring[J].Tribology International, 2010, 43(1):113-128
[8]唐琴,章易程,林晨岚等.凸轮磨损的研究综述与思考[J].机械传动, 2010, 34(08):95-98
[9] 任伟霞,高一新,季永会.GCr15 钢制凸轮轴材料及加工工艺优化[C]//2012 船舶材料与工程应用学术会议论文集. 2012.
[10] 王振廷,孟君晟.摩擦磨损与耐磨材料[M]. 哈尔滨: 哈尔滨工业大学出版社, 2013.
[11] EMDE F.灰铸铁凸轮轴表面重熔硬化[J]. 国外汽车, 1981, 6: 008.[J].世界汽车, 1981, 12(6):52-57
[12] Vaccari J A.激光熔化提高凸轮轴耐磨性[J]. 国外机车车辆工艺, 1993 (6): 39-40.[J].国外机车车辆工艺, 1993, 24(6):39-40
[13] 杜军,刘耀辉.铸铁凸轮轴制造技术及国内外发展动态[J]. 汽车工艺与材料, 1999 (3): 1-4.[J].汽车工艺与材料, 1999, 14(3):1-4
[14]米国发,何斌锋,王狂飞.铸铁凸轮轴铸造技术及发展[J].热加工工艺, 2008, 37(11):99-103
[15] 何斌锋,刘凯.激冷铸铁凸轮轴铸造技术[J]. 金属加工: 热加工, 2009 (5): 58-61.[J].金属加工: 热加工, 2009, 60(3):58-61
[16]刘克明,张友亮,康林萍,等.铸铁凸轮轴的发展现状与展望[J].江西科学, 2011, 29(5):616-620
[17] 杨伯荣,张征权,贾宝春,等.球铁凸轮轴表面氩弧重熔硬化工艺及其试验装置的研究[J]. 汽车工艺与材料, 1987, 3.[J].汽车工艺与材料, 1987, 2(3):9-12
[18]丁阳喜,刘志方,黄志超,等.柴油机奥贝球铁凸轮轴工作可靠性试验研究[J].华东交通大学学报, 2002, 19(4):54-56
[19]丁阳喜.内燃机车奥贝球铁凸轮轴激光表面强化试验研究[J].热加工工艺, 2007, 36(22):76-78
[20]刘宏,郭荣新,张金东.稀土镁球墨铸铁凸轮轴激光热处理的研究与应用[J].山东轻工业学院学报: 自然科学版, 2001, 15(1):43-46
[21]尹晨.凸轮轴工作表面强化处理工艺的研究[J].小型內燃机与摩托車, 2007, 36(2):80-83
[22] 高长安,夏军生,谭文清,等.15CrNi6E钢凸轮轴段深层渗碳工艺[C]// 重庆市机械工程学会热处理分会、重庆市热处理行业协会2012年热处理学术年会. 2012.
[23]贾晶,陆占余.钢凸轮轴激光表面合金化实验[J].山西大学学报: 自然科学版, 1999, 22(1):26-29
[24] 罗兆良.凸轮轴高频淬火感应器的改进[J]. 汽车技术, 1978, 6: 009.[J].汽车技术, 1978, 9(6):48-48
[25] 冀川.钢质凸轮轴的制造新工艺[J]. 汽车工艺与材料, 1987, 3: 011.[J].汽车工艺与材料, 1987, 2(3):41-41
[26] 熊根秀.A-10C 凸轮轴表面淬火工艺的改进[J]. 金属热处理, 1988, 8: 009.[J].金属热处理, 1988, 31(8):39-41
[27] Lengyel J S,宋进桂.钢凸轮轴磨后淬火的新工艺[J]. 车用发动机, 1990, 2: 005.[J].车用发动机, 1990, 13(2):31-34
[28] 朱海丽,耿建忠,邵立新,等.两种不同凸轮轴加工工艺的比较分析[J]. 内燃机, 2010 (2): 24-26.[J].内燃机, 2010, 26(2):24-26
[29] 龙建勇.合金钢凸轮轴的加工工艺[J]. 现代零部件, 2011 (4): 74-78.[J].现代零部件, 2011, 9(4):74-78
[30]董世运,张晓东,徐滨士,等.钢凸轮轴磨损凸轮的激光熔覆再制造[J].装甲兵工程学院学报, 2011, 25(2):85-87
[31] 刘文今,赵海云.45 钢凸轮表面的激光熔凝—合金化复合强化新工艺[J]. 车用发动机, 1996 (5): 51-54.[J].车用发动机, 1996, 19(5):51-54
[32] 张祝君.492 汽油机凸轮轴预先热处理工艺的研究[J]. 汽车工艺与材料, 1998 (4): 20-23.[J].汽车工艺与材料, 1998, 13(4):20-23
[33]Wang S Q, Wang L, Zhao Y T, et al.Mild-to-severe wear transition and transition region of oxidative wear in steels[J].Wear, 2013, 306(1):311-320
[34] Das S, Prasad B K, Jha A K, et al.Three-body abrasive wear of 0.98% carbon steel[J]. Wear, 1993, 162: 802-810.[J]., 1993, (162):802-810
[35]Moore M A.The relationship between the abrasive wear resistance, hardness and microstructure of ferritic materials[J].Wear, 1974, 28(1):59-68
[36] 李泉华,张祝君.合金铸铁凸轮轴氩弧重熔淬火硬化层的磨损试验研究[J]. 金属热处理, 2001 (1): 13-16.[J].金属热处理, 2001, 44(1):13-16
[37] 黄培云.粉末冶金原理[M]. 北京: 冶金工业出版社, 2011.
[38] 刘勇兵,李月英,曹占义等.装配式粉末冶金中空凸轮轴凸轮材料及其制备处理方法[P]. 吉林:CN1858288,2006-11-08.
[39] Michael L.Marucci,George Fillari,Patrick King,K.S.Narasimhan,韩凤麟. 现行烧结-硬化工艺回顾[J]. 粉末冶金技术,2009,02:148-152.[J].粉末冶金技术, 2009, 28(2):148-152
[40] Michael C.Baran,Philip J.Winterton,Thomas E.Haberberger等. 烧结硬化材料在现代汽车齿轮、链轮、凸轮中的应用[J]. 粉末冶金技术,2010,05:387-391.[J].粉末冶金技术, 2010, 23(5):387-391
[41] 铃木保雄,施林康.粉末金属凸轮轴[J]. 国外汽车,1987,04:42-46.[J].国外汽车, 1987, 18(4):42-46
[42]韩凤麟.粉末冶金铁基零件的烧结-硬化处理[J].粉末冶金工业, 2014, 24(1):1-8
[43]梁雪冰,李改,王林山,等.粉末冶金烧结硬化凸轮材料的摩擦磨损性能研究[J].粉末冶金技术, 2015, 33(2):83-88
[44] 刘勇兵,李月英,曹占义.铁基粉末冶金材料的摩擦学特性研究[C]//第二届全国工业摩擦学大会暨第七届全国青年摩擦学学术会议会议论文集. 2004.
[45] 李月英.表面强化铁基粉末冶金材料的摩擦磨损特性研究[D]. 吉林大学, 2004.
[46] Hashimoto K, Ushitani K, Shibata M, et al.Anti-wear ferrous sintered alloy: U.S. Patent 3,977,838[P]. 1976-8-31.
[47] Oaku T, Shioda M, Suzuki S, et al.Wear-resistant sintered ferrous alloy and method of producing same: U.S. Patent 4,556,533[P]. 1985-12-3.
[48] Takagi Y, Katsui Y, Endo H, et al.Wear-resistant, sintered iron alloy and process for producing the same: U.S. Patent 4,702,771[P]. 1987-10-27.
[49] Fujita Y, Kawai S, Takeguchi S.Assembled cam shaft: U.S. Patent 5,007,956[P]. 1991-4-16.
[50]李月英,刘勇兵,陈华.激光表面淬火后铁基烧结凸轮的组织与性能研究[J].粉末冶金技术, 2006, 24(4):280-282
[51] Xu G H, Liang H, Liu J J, et al.Engine Tribology and Surface Modification Technology. J[J]. Heat Treatment of Metals, 2006, 31: 1-11.[J].金属热处理, 2006, 49(31):1-11
[52]刘芳,周科朝,李志友.高合金铁基粉末冶金材料摩擦磨损性能的研究[J].材料科学与工艺, 2011, 9(2):92-95
[53] 陈华,李月英,张驰,等.添加微细铬铁粉对烧结钢摩擦磨损性能的影响[J]. 吉林大学学报: 工学版, 2009 (5): 1162-1166.[J].吉林大学学报: 工学版, 2009, 53(5):1162-1166
[54]Prasad B K, Prasad S V.Abrasion-induced microstructural changes during low stress abrasion of a plain carbon (05% C) steel[J].Wear, 1991, 151(1):1-12
[55]Katsuki F, Yonemura M.Subsurface characteristics of an abraded Fe-04 wt% C pearlitic steel: A nanoindentation study[J].Wear, 2007, 263(7):1575-1578
[56]沈保罗,高见,王艳戎,等.处理对合金灰铸铁凸轮轴耐磨性的影响[J].现代铸铁, 2008, 28(3):74-77
|
|
|
|