Effect of sintering temperature on properties of iron-based powder sintered products |
SU Fengge1.,SHANG Shubo2.,ZHANG Ruiping3.,ZHENG Zhuo4.,SHANG Yanjing1. |
(1.Zhejiang Baida precision manufacturing Co., Ltd., Taizhou 317700, China;2.Liaoning Equipment Manufac‐
turing Vocational and Technical College, Shenyang 110161, China;3. Jiande Municipal Food and Drug Inspec‐
tion and Testing Center, Hangzhou 311600, China;4.Hangzhou Yitong New Materials Co.,Ltd., Hangzhou
311613, China) |
|
|
Abstract In this paper, Fe-Cu-C, Fe-Cu-Ni-Mo-C and Fe-Mo-C green were sintered at five different tempera‐
tures of 1 100, 1 140, 1 180, 1 200 and 1 220 ℃ in a powder metallurgy industrial furnace. The metallographic
and fracture morphology were observed by metallographic microscope and scanning electron microscope(SEM).
The effects of different sintering temperatures on the hardness, fracture strength, metallography and fracture mor‐
phology of the samples were studied. The experimental results show that temperature at 1 100 ℃ and 1 140 ℃
have little influence on the hardness and strength of the above alloy between 1 100 ℃ and 1 220 ℃, the fracture
strength of Fe-Mo-C and Fe-Cu-Ni-C increases with the increase of sintering temperature. When the sintering
temperature exceeds 1 180 ℃, the fracture strength of Fe-Cu-C materials decreases with the increase of sintering
temperature.
|