Effect of pore forming agent content on porous nickel plate prepared by powder rolling |
YIN Quanzhong1,LI Xiaoqiang1,LIANG Yongren2,LI Rong2,REN Shangyuan2,
KANG Zhixin1 |
(1. School of Automotive and Mechanical Engineering, South China University of Technology, Guangzhou
510640, China; 2. Western Baode Technologies Co., Ltd, Xi’an 710201, China) |
|
|
Abstract Porous nickel plates with porosity of 22.2%-52.4% were prepared by powder rolling technology using
ammonium bicarbonate(NH4HCO3)as pore-making agent. The effect of pore-forming agent content on microstructure
and properties of porous nickel plate was studied. The results show that with the increase of pore-forming
agent content, the porosity of porous nickel plate increases gradually, the relative permeability increases gradually,
and the tensile strength decreases gradually. When the content of pore-forming agent is 20%, the porosity of porous
nickel plate is 40.7%, the relative permeability coefficient is 10.79 m3/(h·kPa·m2), and the tensile strength is
135 MPa. When the content of pore-forming agent is 40%, the porosity of porous nickel plate is 52.4%, the relative
permeability coefficient is 41.0 m3/(h·kPa·m2), and the tensile strength is reduced to 51 MPa.
|
Received: 02 March 2023
|
|
|
|
|
|
|