Effects of Cr addition on microstructure and mechanical properties of powder metallurgy Ti-6Al-4V alloy |
XU Jian1, WANG Wen-yan1,2, ZHANG Hao-yin1, XIE Jing-pei1,2, LI Luo-li1 |
1. School of Material Science and Engineering, He’nan University of Science and Technology, Luoyang 471003, China 2. He’nan Key Laboratory of Non-Ferrous Materials Science and Processing Technology, Luoyang 471023, China |
|
|
Abstract Ti-6Al-4V alloy with different Cr content was prepared by the method of cold isostatic pressing and vacuum sintering. The effect of Cr addition on the microstructure and mechanical properties of Ti-6Al-4V alloy was investigated using optical microscope, mechanical properties testing and scanning electron microscope. The results show that the compound TiCr2 does not appear in the alloy after adding Cr element, and the alloy is composed of (α+β) phase, which belongs to widmanstatten structure. The addition of Cr element makes the relative density of the alloy decrease and the compressive strength increase. The compressive strength of the alloy is 1 855 MPa when Cr content is 4wt%. The fracture mode of alloy is ductile fracture when Cr content is 1wt% and 2wt%; while the fracture mode turns to dissociative fracture when Cr content is 3wt% and 4wt%.
|
Received: 15 January 2014
Published: 18 December 2014
|
|
|
|
[1] |
侯红亮,李志强,王亚军,等.钛合金热氢处理技术及其应用前景[J].中国有色金属学报,2003,13(3): 533-549.
|
[2] |
曹春晓.一代材料技术,一代大型飞机[J].航空学报,2008,29(3)701-706.
|
[3] |
汤慧萍,刘咏,韦伟峰,陈丽芳.添加稀土元素对粉末冶金Ti合金显微组织和力学性能的影响[J].中国有色金属学报,2004,14(2):244—249.
|
[4] |
HANSON A D, RUNKLE J C, WIDMER R, HEBEISSEN J C. Titanium near shapes from elemental powder blends[J]. International Journal of Powder Metallurgy,1990,26(2):157-164.
|
[5] |
汤慧萍,黄伯云,刘咏,欧阳洪武.粉末冶金钛合金致密化研究进展[J].稀有金材料与工程,2003,32(9):677-680.
|
[6] |
LIU Yong, CHEN Li-fang, WEI Wei-feng, TANG Hui-ping. Improvement of ductility of powder metallurgy titanium alloys by addition of rare earth element[J].Journal of Materials Science and Technology,2006,22(4):465-469.
|
[7] |
Zhang X D, Evans D J, Baeslack W A,et al. Effect of long term aging on the microsrtuctural stability and mechanical properties of Ti-6Al-2Cr-2Mo-2Sn-2Zr alloy. Mater Sci Eng A,2003,344:300-311.
|
[8] |
Huang P Y. Powder Metallurgy Principle . Beijing:Metallurgical Industry Press, 2004:133.
|
[9] |
DUCKWORTH W. Discussion of ryshkewitch paper[J]. Joumal Of American Ceramics Society,1953,36:68-75.
|
|
|
|