Study on oxidation behavior of SiC particles |
LI Min1,WANG Ai-qin1,2,XIE Jing-pei1,SUN Ya-li1 |
1. College of Material Science and Engineering, He’nan University of Science and Technology, Luoyang 471023, China 2. Collaborative?Innovation?Center?of?Non-Ferrous?Metals,?He’nan Province, Luoyang 471023, China |
|
|
Abstract The changes of microstructure and elements in SiC particles before and after oxidation were studied; the oxidation weight gain trend and influencing factors were also presented. The results show that, oxidation reaction makes the morphology of SiC particles changed greatly, which has passivation effect on the SiC particles, and makes SiC particles lose sharp edges, tending to be smoother. SiO2 forms on SiC particles surface after oxidation. During the early oxidation stage, the weight of SiC increases with the increasing oxidation temperature and oxidation time, the oxidation rate is mainly controlled by the interfacial chemical reaction rate. During later oxidation stage, the weight of the SiC increases slowly, and the oxidation rate is controlled by the diffusion rate of O2 and CO in the surface oxide film. A simple estimation formula for oxide thickness of SiC particles was proposed.
|
Received: 24 March 2015
Published: 01 February 2016
|
|
|
|
[1]宁向梅, 高积强.反应烧结SiC材料的高温氧化行为研究[J].耐火材料, 2001, (5):270-272
[2]李玉海, 黄晓莹, 王承志, 李颖.颗粒的高温氧化动力学[J].材料研究学报, 2009, 23(06):582-586
[3]王传廷, 马立群, 尹明勇, 刘真云, 丁毅, 张华, 陈育贵.氧化处理对_复合材料润湿性和界面结合的影响[J].特种铸造及有色合金, 2010, 30(11):1062-1065
[4]朱庆山, 邱学良, 马昌文.高温氧化的热力学研究[J].计算机与应用化学, 1996, 13(02):91-96
[5]房国丽, 李进, 杨智春.复合材料界面反应的热力学分析[J].宁夏工程技术, 2007, 6(01):76-79
[6]霍玉柱, 商庆杰, 潘宏菽.高温氧化的研究[J].半导体技术, 2010, 35(10):980-982
[7]刘凤国.SiC颗粒增强铝基复合材料增强体颗粒预处理及复合工艺研究[D].沈阳理工大学, 2010.
[8]刘俊友,刘英才,刘国权.颗粒氧化行为及铝基复合材料界面特征[J].中国有色金属学报, 2002, 12(05):961-966
[9]高瑛.Sialon/Si_3N_4-SiC系材料中高温氧化行为的研究[D].西安建筑科技大学, 2007.
|
|
|
|