Experimental study on the preparation of ultrafine zinc powder by hot-dip galvanizing slag |
BU Er-jun1,2,3,XUE Xiang-xin1,3,YANG He1,3 |
1. Department of Resources and Environment, School of Metallurgy, Northeastern University, Shenyang 110819, China 2. Technology Center, Handan Iron and Steel Company, HBIS, Handan 056015, China 3. Institute of Metallurgical Resources and Environmental Engineering, Northeastern University, Shenyang 110819, China |
|
|
Abstract The hot galvanizing slag from cold rolling mill was used as raw materials, ultrafine zinc powder was prepared by evaporation condensation method. Using new evaporation device and cooling device, effects of maximum evaporation temperature, temperature holding time, protective gas quantity, evaporation materials and cooling intensity on the yield of zinc powder and particle size distribution were studied. The resulting particle size distribution, chemical composition, XRD and microstructure of the ultrafine zinc powder were tested, and the causes and countermeasures of zinc powder conglobation were discussed.
|
Received: 23 September 2015
Published: 29 August 2016
|
|
|
|
[1]谭和荣.浅析超细高活性锌粉的制备和用途[J].有色冶炼, 2002, (2):11-13
[2].范红喜.高性能涂料级锌粉塔式炉生产实践[D].长沙:中南大学,2004.
[3]刘全民,王彦军,张鑫,等.锌粉制备技术现状与趋势[J].南方金属, 2015, (202):1-3
[4]陈文汨,万新华,孙英樱.制备雾化锌粉技术研究[J].材料导报, 2000, 14(12):59-61
[5]王凤朝.锌粉生产工艺选择分析[J].有色冶金设计与研究, 2013, 34(6):26-28
[6]贺惠生,梁进..超细锌粉的生产与应用[J].有色金属(冶炼部分), 1998, (10):41-44
[7]袁训华.热浸镀锌渣蒸发—凝聚法制备锌粉的工艺理论及设备原理研究[D] .昆明:昆明理工大学,2007.
[8]陆必志,陈振兴.蒸发-冷凝法制备超细鳞片状锌粉[J].粉末冶金工业, 2005, 15(2):5-8
[9]吴浩.精馏冷凝锌粉的生产与分级[J].有色冶炼, 2000, 29(5):21-23
[10]王子谦..精馏塔生产锌粉[J].有色金属(冶炼部分), 1992, (5):5-11
[11]蔡晓兰,林兴铭,王国富..用高能球磨制备超细鳞片状锌粉[J].世界有色金属, 2004, (4):48-49
[12]胡会利,李宁,程瑾宁,等.电解法制备超细锌粉的工艺研究[J].粉末冶金工业, 2007, 17(1):24-29
[13]侯新刚,王胜,王玉棉.超细活性锌粉的制备与表征[J].粉末冶金工业, 2004, 14(1):10-14
[14]李永祥,黄梦阳,任锐..电解法制备树枝状锌粉的工艺研究[J].四川有色金属, 2011, (3):45-50
[15]林峰,雷晓旭,王进保,等.超细锌粉的制备及其应用前景[J].材料保护, 2013, 46(5):48-51
[16]王子谦,王乐津..锌锭反射炉法生产锌粉实践[J].有色冶炼, 1998, (1):20-21
[17]东北大学.一种用于易挥发粉末金属冶炼的反应罐:中国,201320530307.3 [P].2014-02-26.
[18]熊秦.火法炼锌过滤式冷凝器:中国,200620022458.8 [P].2007-12-06.
[19]河北钢铁股份有限公司邯郸分公司.一种生产超细锌粉的可拆卸冷凝装置:中国,201320589901.X[P].2014-04-09.
[20].袁训华,何明奕,张启富.热镀锌渣制备锌粉的试验研究[C].北京:第7届亚太镀锌大会,2007:243~246.
[21]刘剑.粉体团聚的控制措施[J].粉末冶金工业, 2015, 25(4):54-57
|
|
|
|