Effect of pre-deformation on heat treatment microstructure of FGH97 PM superalloy |
HAN Shou-bo1,2,Lü Ri-hong3,ZHANG Ying1,2,SUN Zhi-kun1,2,LI Ke-min1,2,HUANG Hu-bao1,2,LIU Ming-dong1,2,ZHANG Yi-wen1,2 |
1. Beijing CISRI-Gaona Materials & Technology Co., Ltd., Beijing 100081, China 2. High Temperature Materials Research Institute, CISRI, Beijing 100081, China 3. Guizhou Liyang Aviation Dynamic Co., Ltd., Aviation Industry of China, Guiyang 561102, China |
|
|
Abstract During the production and processing process, local surface pits usually occur on FGH97 PM superalloy products due to improper operation. The FGH97 alloy product with this kind of defects was tested and analyzed. The abnormal grain coarsening was found at the deformation zone caused by external force. Thermal simulation experiments were carried out to verify the effect of pre-deformation on heat treatment microstructure of FGH97 alloy. Results show that abnormal grain growth appears during heat treatment when the deformation of FGH97 alloy reaches the critical deformation, resulting in non-homogeneous microstructure, thereby affecting the performance and application of the alloy. It is advised that operation specification should be strictly abided to avoid local deformation.
|
Received: 19 August 2016
Published: 15 December 2016
|
|
|
|
[1] 雷景富, 郑勇, 余俊, 等. 镍基粉末高温合金的研究进展[J]. 宇航材料工艺, 2011, 41(6): 18-22.[2] 刘建涛, 张义文, 陶宇, 等. FGH97合金的显微组织[J]. 材料热处理学报, 2011, 32(3): 47-51.[3] Shen Yu, Yu Hu-ping, Ruan Xue-yu, et al. Discussion and prediction on decreasing flow stress scale effect [J]. Transactions of Nonferrous Metals Society of China, 2006, 16(1): 132-136.[4] 郭婧, 姚志浩, 董建新, 等. 高温合金中晶粒异常长大及临界变形量研究进展[J]. 世界钢铁, 2011, 11(4): 38-45,67.[5] 吕炎, 曲万贵, 陈宗霖, 等. 临界变形粗晶形成机理的探讨[J]. 金属学报,1986, 22(6): A489-A493, Plate A54-55.[6] 王从曾. 材料性能学[M]. 北京: 北京工业大学出版社, 2007.[7] 刘天佑. 奥氏体混晶对钢的力学性能的影响[J]. 本溪冶金高等专科学校学报, 2003, 5(3): 1-5. |
|
|
|