Study on properties of Ni based+WC coating by plasma spray welding |
ZENG Zhi-qiang,ZHANG Bo,WANG Jun-yuan,ZHU Xi-jing,GUI Kai |
School of Mechanical Engineering and Automation, North University of China, Taiyuan 030051, China |
|
|
Abstract In order to reduce the severe friction and abrasion between diesel engine pistons and cylinder sleeves working under high temperature and high pressure and enhance the heat resistance and corrosion resistance, 15%, 25% and 35% (mass percent) of WC powder as the strengthening materials were mixed into the Ni45 powder and Ni55 powder to manufacture the hard-face layer on the surface of 38CrMoAl diesel engine cylinder sleeves by plasma spray welding technology, respectively. The properties of the hard-face layer including the micro-structure, micro-hardness and thermal physical parameters were analyzed and tested. Results show that all hard-face layer prepared by the above 6 kinds of powder can play the role of strengthening, but the hard-face layer with the best comprehensive performance was produced by (Ni45+25%WC, mass percent) alloyed powder, in which the micro-hardness exceeds 600 HV, the gradient micro-hardness and the coefficient of thermal expansion match the substrate and meet the requirements of strengthening the inner wall of the cylinder sleeves.
|
Received: 07 July 2016
Published: 28 March 2017
|
|
|
|
[1] Zeng, Zhi-Qiang, Wang, Hua-Chang, Wang, Hong-Fu, Wang, Jun-Yuan. Preparation of Ni60-Cr3C2 coating by plasma spraying, plasma Re-melting and plasma spray welding on W6Mo5Cr4V2[J]. Journal of Wuhan University of Technology, 2012(02): 389-393.[2] 李承娣,沈岩,王永彬等.化学刻蚀高硅铝合金缸套的摩擦磨损性能[J].中国表面工程,2014,06:104-109.[3] Wang Junyuan , Wang huachang , Wang Hongfu , Zeng Zhiqiang .Preparation of Ni60-WC Coating by Plasma Spraying, Plasma Re-melting and Plasma Spray Welding on Surface of Hot Forging Die [J].Journal of Wuhan University of Technology-Mater,2012,08:640-643.[4] Piao Zhongyua , Xu Binshi , Wang Haidou , Wen Donghui . Influence of surface nitriding treatment on rolling contact behavior of Fe-based plasma sprayed coating[J] . Applied Surface Science ,2013,266:420-425.[5] Huan Zhang , Youtao Xie , Liping Huang , Shansong Huang , Xuebin Zheng , Guang Chenb. Effect of feedstock particle sizes on wear resistance of plasma sprayed Fe-based amorphous coatings [J]. Surface & Coatings Technology ,2014,258: 495-502[6] JIANG Chaoping,WANG Junxin. Effect of Laser Remelting on the Microstructure and Corrosion Resistance of Plasma Sprayed Fe-based Coating[J]. Wuhan University of Technology and SpringerVerlag Berlin Heidelberg,2015,08:04-07.[7] Piao Zhongyu,Xu Bingshi .Characterization of Fe-based alloy coating deposited by supersonic plasma spraying[J].Fusion Engineering and Design ,2013,09:2933-2938.[8] 王守忠,刘玉莹.气缸套表面等耐磨处理可行性研究[J].制造技术与机床,2008(9):34-37. |
|
|
|