Cobalt enriched wlag from the low acidic leaching of spent li-ion batteries by sulfuting roasting and leaching |
ZHOU Rong-chao, LU Jun-que, YE Min-jie, WANG Yu-bin, WANG Du |
Hu’nan Brunp Recycling Technology Co. ,Ltd. , Changsha 412600, China) |
|
|
Abstract Cobalt was recovered from the low acidic leaching residue of spent lion batteries by sulfating roasting-leaching process. X-ray diffraction shows that Co3O4 is the main phase of raw materials that is difficult to leach. The results show that nearly 99.86% of cobalt is leached out under optimal conditions, the roasting temperature is 350 ℃, H2SO4-to-raw material mass ratio is 0.8, and roasting time is 1 h.
|
Received: 15 December 2018
|