Preparation and properties of porous nickel by space-holder-method |
WANG Hongwei1,LI Yonghua1,ZHENG Qingsong1,CHEN Xiaolong1,2 |
(1.Shangi Institute For Advanced Materials(Nanjing)CO., LTD. Nanjing Jiangsu 210046. China; 2. Nanjing
Tech University Nanjing Jiangsu 211816. China) |
|
|
Abstract Porous nickel with high porosity and small pore was fabricated by powder metallurgy which was called
space-holder-method and adding sodium chloride(NaCl). The pore structures and mechanical properties were
examined. The results show that by Adjusting the proportion of space-holder, sintering temperature and cooling
time, porosity of sample was 60.84%~64.92%, the mean pore size was 0.20-8.80 μm with the proportion of over 20
μm occupying 92.0%~96.1%, compressive strength was 8.9-13.4 MPa. The mean pore size decreases correspondingly
with increase of cooling time, but the compressive strength take on the trend of increase.
|