Characterization of H13 alloy special powders prepared by plasma rotating electrode atomization |
QIAO Zhenxing1,LIU Zenglin2,ZHANG Dejin1,2,SUN Jing1,CHEN Linlin1,
KAN Hongcheng2 |
(1. Shandong Luyin New Material Technology R&D Co. Ltd., Jinan 250100, China; 2. Shandong Luyin New
Material Technology Co. Ltd., Gangcheng 271104, China) |
|
|
Abstract This paper describes a production process for the preparation of H13 alloy special powders by plasma
rotating electrode atomization (PREP), including raw material preparation, atomization, and powder grading. The
morphology, particle size, composition, fluidity and bulk density of the powder were tested by using scanning
electron microscope, particle size analyzer, nitrogen-sulfur meter, ICP, Hall flow meter and bulk density meter.
And a comparison was made with the powder produced by a domestic company using aerosolization (AA). The
result shows that the surface quality of H13 alloy powder produced by PREP is excellent, with high powder sphericity,
clean surface and almost no satellite powder, adhesive powder and hollow powder. The surface morphology
is mainly fine dendritic organization with uniform organization. The physical properties of the powder are excellent,
with high bulk density (4.6 g/cm3) and good flowability (12.8 s/50g). The particle size of the powder is
centrally distributed, and the yield of the powder of specific size is high. However, the yield of fine powder is not
high, and further optimization of the process is needed. The surface quality of H13 alloy powder prepared by AA
is poor, with more satellite powder, shaped powder and adherent powder, and more surface defects. In addition,
the physical properties are poor, and the fluidity and bulk density are not as good as the requirements of powder
products.
|
Received: 19 September 2023
|
|
|
|
|
|
|