| Process study of Al2O3 dispersion strengthened copper powders prepared with waste cupric liquor |
| SHI Yong-liang1，LIN Tao2，YANG Xiao-cai1，SHI Yan-lin1，LI Xiu-min1 |
1.Department of Materials Engineering， Hebei College of Industry and Technology， Shijiazhuang 050091， China
2. Advanced Material and Technology Institute， University of Science and Technology Beijing， Beijing 100083， China |
|
|
|
|
Abstract Using acidic and alkaline waste cupric liquor as raw material， the copper solution was prepared with the processes of acid and alkali neutralization， filtration and sulfuric acid dissolution. Then， the soluble aluminum salt was added into the copper solution. Finally， the nano-Al2O3-dispersed strengthening copper-based powders with 2% (mass percent) alumina were prepared with the methods of complex chemical co-precipitation， calcination and hydrogen reduction. The Cu2+ content in filtrate was measured by flame atomic absorption spectrometry， and the influences of mixing ratio of acidic and alkaline waste cupric liquor on the Cu2+ extraction efficiency were studied. The particle size， morphology and composition of precursor powder， Al2O3-CuO composite powder， Al2O3-Cu powder and Al2O3 dispersed phase were analyzed through scanning electron microscope and X-ray diffraction. The calcination and hydrogen reduction processes were analyzed with TG-DTA test. The results show that， neutralization reaction is completed fully when acidic and alkaline waste cupric liquor has the volume ratio of 2 to 3， and Cu2+ extraction efficiency is 96.75% (mass percent). Precursor powder with fine particle size and no agglomeration is obtained by the way of rapid?precipitator addition. The optimum calcination and hydrogen reduction temperature is 500 ℃ and 550 ℃， respectively. The dispersion phase distributes uniformly and the particle size is less than 200 nm. The extraction experiments prove that the dispersed phase is nano Al2O3.
|
|
Received: 29 February 2016
Published: 18 April 2017
|
|
|
|
| [1] 潘超, 秦海, 青吕智. 并流共沉淀法制备铜锡镧复合预合金粉末的研究[J]. 超硬材料工程, 2010, (2) 22: 35-39[2] 慕光杉, 蒋毅民. 含铜蚀刻废液的回收与利用[J]. 安全与环境工程, 2006,(3)13:66-68[3] 温炎, 陈昌铭, 陈志传. 利用含铜蚀刻废液生产碱式碳酸铜[J]. 化工环保，2004, (2) 24: 131-133.[4] Seung Ju Han, Ji Hwan Song, Yongju Bang, et al. Hydrogen production by steam reforming of ethanol over mesoporous Cu-Ni-Al2O3-ZrO2 xerogel catalysts[J]. International Journal of Hydrogen Energy. 2016, 4(41): 2554-2563[5] SahaR K, WeibS. A comparison of microstructural developments in TLP diffusion bonds made using ODS N i alloys[J]. Materials Science and Engineering, 2005, 21(7): 319-327.[6] 符学龙, 丁红燕, 戴起勋. 共沉淀法制备纳米CuO/Al2O3复合粉体[J]. 机械工程材料, 2007, 5(31): 30-33[7] Zhang XueHui, Li XiaoXian, Chen Hao, et al. Investigation on microstructure and properties of Cu-Al2O3 composites fabricated by a novel in-situ reactive synthesis[J]. Materials & Design, 2016, (15)92: 58-63[8] 黄劲松, 甘子旸, 张仲灵. ODS 弥散强化铜合金[J]. 2014, 3(34): 108-111 |
|
|
|
2017, Vol. 27 