| Wear Resistance of WC-12Co Coating Prepared by High Velocity Oxygen Fuel Spraying |
| WU Xu1, GUO Zhi-meng1, YU Ji-ping2 |
1. School of Materials Science and Engineering, University of Science Technology Beijing, Beijing 100083, China
2. AVIC Xi’an Aero-Engine Group Limited Company, Xi’an 710021, China |
|
|
|
|
Abstract WC-12Co coating was prepared by high velocity oxygen fuel (HVOF) spraying technology. The coating porosity, micro-hardness and the bonding strength between the substrate and coating were measured by IA32 quantitative analysis software, LM700AT automatic micro-hardness tester and universal testing machine, respectively. In addition, the tribological properties of the coating were tested on MRH-3 high-speed ring-on-block machines. The results show that the coating porosity is 0.33%, the micro-hardness is 1 393 HV, and the coating adhesive strength is higher than 64.4 MPa. With the test load of 800 N, the rotate speed of 1 000 r/min, the friction pair of GCr15, the experimental period of 1 h and the Great Wall CJ-4 15W/40 as lubricating oil, the friction coefficient of the coating remains at 0.099, the weight loss of the coating is 0.001 6 g. The wear mechanism is abrasive wear.
|
|
Received: 12 March 2014
Published: 08 August 2014
|
|
|
|
| [6] |
王卫泽, 李长久.热喷涂涂层的结构及其表征[J].[J].材料保护,, 2006, 39(11):43-47
|
| [11] |
李行志, 胡树兵.等离子喷涂层组织结构及磨损性能研究[J].湖北汽车工业学院学报, 2005, 19(3):35-37
|
| [1] |
Sidhu.T.S,Prakash[J].S, and Agrawal. R.D. Studies on the properties of high-velocity oxy-fuel thermal spray coatings for higher temperature applications [ J ] . Materials Science, 2005, 41(6):805-823
|
| [2] |
范毅, 丁彰雄, 张云乾.纳米涂层在轴流式引风机叶片防磨上的研究[J].武汉大学学报, 2006, 39(3):135-138
|
| [3] |
庄军.HVOF-热喷涂领域的新成员[J].[J].机车车辆工艺, 1997, ( 6):28-30
|
| [4] |
周贻茹, 施昌勇, 许亚兰.超音速火焰喷涂-宇航材料研究的重要工艺[J].[J].宇航材料工艺, 1996, (3):58-61
|
| [5] |
韩志海, 徐滨士, 王海军.三种超音速热喷涂工艺制备-涂层的组织结构分析[J].中国表面工程, 2005, 18(3):23-27
|
| [7] |
张天明.超音速火焰喷涂涂层的组织性能研究[J].热加工工艺, 2007, 36(11):48-49
|
| [8] |
Li H, etal.Young’s modulus and fracture toughness determination of high velocity oxy-fuel-sprayed bioceramic coatings [J].[J].Surf Coat Techn,, 2002, , 155:21-25
|
| [9] |
简中华, 马壮, 王富耻, 曹素红, 王全胜.超音速火焰喷涂-涂层耐磨性研究[J].润滑与密封, 2007, 32(l):90-98
|
| [10] |
YANG Q, SENDA T, OHMORI A.Effect of carbide grain size on microstructure and sliding wear behavior of HVOF-sprayed WC-12Co coatings[J].Wear, 2003, 254(12):23-34
|
|
|
|
2014, Vol. 24 