| Fe74Al4Sn2P10Si4B4C2 Bulk Amorphous Rods and Tube Prepared by Water-Cooled Copper Mold Method |
| CHEN Fei-fei, ZHOU Shao-xiong |
| National Amorphous and Nanocrystalline Alloy Engineering Center, China Steel Institute of Science and Technology Corporation, Beijing 100081,China |
|
|
|
|
Abstract Bulk amorphous rods of Fe74Al4Sn2P10Si4B4C2 alloy with diameter of 1.0mm, 1.5mm and 2.0mm were prepared by water-cooled copper mold method. The magnetic properties of the rods were measured by vibrating sample magnetometer, which showed high saturation magnetic induction and low coercive force. Bulk amorphous tube (5 mm×7 mm×15 mm) of Fe74Al4Sn2P10Si4B4C2 alloy was also prepared by water-cooled copper mold method, which showed similar thermal properties with bulk amorphous rods. It was indicated that Fe74Al4Sn2P10Si4B4C2 alloy had good castability.
|
|
Received: 23 January 2014
Published: 28 April 2014
|
|
|
|
| [2] |
H.W.Kui,DTurnbull. Melting of Ni40Pd40P20 glass[J].Appl. Phys. Lett., 1985, 47(8):796-797
|
| [3] |
N.Nishiyama,AInoue. Glass transition behavior and viscous flow working of Pd40Cu30Ni10P20 amorphous alloy[J].Mater. Trans, JIM., 1999, 40(1):64-71
|
| [4] |
A.Inoue,MKohinata,A. Tsai,et al. Mg-Ni-La amorphous alloys with a wide supercooled liquid region[J].Mater. Trans, JIM, 1989, 30(5):378-381
|
| [6] |
C.Fan, A. Inoue. Shear sliding-off fracture of bulk amorphous Zr-based alloys containing nanoscale compound particles[J]. Mater. Trans, JIM. 1999, 40(12):1376-1381
|
| [7] |
A.Inoue,HYamaguchi,T. Zhang,et al. Al-La-Cu amorphous alloys with a wide supercooled liquid region[J].Mater. Trans, JIM., 1990, 31(2):104-109
|
| [8] |
A.Inoue, Y. S. Gook. Fe-base ferromagnetic glassy alloys with wide supercoooled liquid region[J]. Mater. Trans., JIM, 1995, 36:1180-1183
|
| [11] |
A.Inoue, A. Takeuchi, T. Zhang. Ferromagnetic bulk amorphous alloys[J]. Metall. Mater. Trans., 1998, A29:1779-1793
|
| [12] |
A.Inoue, T. Zhang, T. Itoi. New Fe-Co-Ni-Zr-B amorphous alloys with wide supercooled liquid region and good soft magnetic properties[J]. Mater. Trans., JIM., 1997, 38:359-362
|
| [13] |
A.Inoue, M. Koshiba, T. Zhang, et al. Wide supercooled liquid region and soft magnetic properties of Fe56Co7Ni7Zr0-10Nb(or Ta)0-10B20 amorphous alloys[J]. J. Appl. Phys., 1998, :1967-1974
|
| [15] |
W.Zhang, A. Inoue. Thermal and magnetic properties of Fe-Co-Ln-B(Ln=Nd, Sm, Tb, Dy) with high magnetostriction[J]. Mater. Trans, JIM., 1999, 40:78-81
|
| [16] |
A.Inoue,ATakeuchi,B.L.Shen. Formation and functional properties of Fe-based bulk glassy alloys[J].Mater. Trans., JIM., 2001, 42(6):970-978
|
| [17] |
门华，杨明川，徐坚.添加Co对Mg65Cu25Y10合金玻璃形成能力的影响[J].材料研究学报, 2002, 16:379-384
|
| [20] |
陈非非，周少雄.铜模吸铸法制备的块体非晶与块体纳米晶合金[J].材料科学与工程学报, 2004, 22(5):630-633
|
| [1] |
H.W.Kui,AL. Greer,D. Turnbull. Formation of bulk metallic glass by fluxing[J].Appl. Phys. Lett., 1984, 45(6):615-616
|
| [5] |
N.H.Pryds,MEldrup,M. Ohnuma,et al. Preparation and properties of Mg-Cu-Y-Al bulk amorphous alloys[J].Mater. Trans, JIM., 2000, 41(11):1435-1442
|
| [9] |
A.Inoue, Y. Shinohara, J. S. Gook. Thermal and magnetic properties of bulk Fe-based glassy alloys prepared by copper mold casting[J]. Mater. Trans., JIM, 1995, 36:1427-1433
|
| [10] |
A.Inoue,AMurakami,T. Zhang.,et al. Thermal stability and magnetic properties of bulk amorphous Fe-Al-Ga-P-C-B-Si alloys[J].Mater. Trans., JIM., 1997, 38(189):196-
|
| [14] |
A.Inoue, W. Zhang. New Fe-based amorphous alloys with large magnetostriction and wide supercooled liquid region before crystallization[J]. J. Appl. Phys., 1999, 85:4491-4493
|
| [18] |
陈伟荣，王英敏，羌建兵.Zr基大块非晶合金成分的等电子浓度和等原子尺寸判据[J].材料研究学报, 2002, 16:219-224
|
| [19] |
甘章华，王敬丰，肖建忠.块体非晶合金Fe-Ni-P-B-Ga的制备与性能[J].金属学报, 2003, 39:1085-1088
|
|
|
|
2014, Vol. 21 