Effect of Pickling Duration on the Surface Integrity of Hot-Rolled Stainless Steel Sheets During Pickling Process |
LI Xiao-liang, SHI Pei-yang, YUE Ying-ying, JIANG Mao-fa |
Key Laboratory for Ecological Metallurgy of Multimetallic Ores Ministry of Education, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
Abstract Electrochemical methods, LSCM and SEM were performed to investigate the effect of pickling duration of hydrochloric acid on the surface integrity of hot-rolled ferritic stainless steel during pickling process. Research showed that as the time duration prolonged, the surface became smoother. However, long immersion duration resulted in local attack at grain boundaries. With the increase of pickling duration, the shapes of polarization curves in weak polarization area kept similar, but the pitting potential and the radiuses of capacitive loop increased first and then decreased. When the pickling duration was 50 s, the corrosion resistance of stainless steel was the best.
|
Received: 14 March 2014
Published: 26 June 2014
|
|
|
|
[5] |
张世红,祁秀玲,匡飞,等.牛黄解毒片在中的缓蚀性能研究[J].腐蚀科学与防护技术, 2010, 22(7):348-350
|
[7] |
闫莹,李伟华,邢少华,等.新型杂环化合物在1mol/LHCl中对Q235钢的缓蚀性能研究[J].腐蚀科学与防护技术, 2007, 19(6):414-419
|
[1] |
Ponto L, Datta M, Landolt D.Electropolishing of iron-chromium alloys in phosphoric acid-sulphuric acid electrolytes[J].Surface and Coatings Technology, 1987, 30(3):265-276
|
[2] |
Narvaez L, Cano E, Bastidas J M.Hydrogen peroxide decomposition in an environmentally friendly picking solution for AISI 316L stainless steel[J].Corrosion Science, 2005, 1(61):21-29
|
[3] |
林百春.不锈钢表面处理酸洗、钝化与抛光[J].材料开发与应用, 2006, 21(3):36-39
|
[9] |
王秀梅,杨怀玉,王福会.两种季铵盐化合物在溶液中对碳钢缓蚀效果的对比研究[J].腐蚀科学与防护技术, 2010, 22(4):338-342
|
[10] |
Wang Xiumei, Yang Huayu, Wang Fuhui.A comparative investigation on inhibition performance of two quaternary ammonium salts for mild steel in 05molL HCl solution[J].Corrosion Science and Protection Technology, 2010, 22(4):338-342
|
[6] |
Zhang Shihong, Qi Xiuling, Kuang Fei, et al.Inhibition performance of bezoar detoxcation tablet for Q235 carbon steel in 1molL HCl[J].Corrosion Science and Protection Technology, 2010, 22(7):348-350
|
[8] |
Yan Ying, Li Weihua, Xing Shaohua, et al.Corrosion inhibition of mild steel by novel heteroerocyclic compound in 1molL HCl solution[J].Corrosion Science and Protection Technology, 2007, 19(6):414-419
|
[4] |
Lin Baichun.Surface treatment of stainless steels: acid pickling,passivation and polishing[J].Development and Application of Materials, 2006, 21(3):36-39
|
|
|
|