Abstract:Adding various contents of Nd2O3 into natural dolomite, magnesium-calcium materials were prepared by two-step calcination method, and the influence of Nd2O3 on sintering properties of dolomite was studied. The results show that the bulk density of samples without Nd2O3 is 3.25 g/cm3, the apparent porosity is 3.8%, and the MgO grain size is 3.82 μm when sintered at 1 600 ℃ for 3 h. When 0.75% (mass percent) of Nd2O3 is added, the activation energy of grain growth is decreased due to the solid solution reaction of Nd2O3 with MgO and CaO. The bulk density of the sample increases to 3.33 g/cm3, the apparent porosity decreases to 2.8%, and the MgO grain size increases to 4.53 μm.
[1] Barbanyagrè V D and Zubakova L E. The water-resistant dolomite briquette with free CaO produced from the Lis’egorskoe deposit dolomite[J]. Ogneup. Tekh. Keram., 1998,10: 12- 14.[2] Antonov G I, Nedosvitii V P, Kulik A S, and Semenko O M. Stabilized dolomite-periclase refractories[J]. Ogneup. Tekh.Keram, 2004( 2): 8 -12.[3] Suvorov S A , Nazmiev M I, Baranov A P, and Dmitrienko A A. A high-density water-resistant magnesia-lime material based on dolomite[J]. Refractories and Industrial Ceramics, 2005, 3(46): 217-219.[4] 顾华志,洪彦若.镁钙材料抗水化性能的研究发展[J]. 炼钢, 2002,4(8): 31-35.[5] Ghosh A, Bhattacharya T K, Mukherjee B, Das S K, The effect of CuO addition on the sintering of lime[J]. Ceramics International, 2001, 27: 201-204.[6] Ghoneim N M, Mandour M A, Serry M A. Sintering of lime doped with La2O3 and CeO2[J]. Ceramics International, 1989, 15: 357–362.[7] Ghosha A, Bhattacharya T K, Maitib S. Densification and properties of lime with V2O5 additions[J]. Ceramics International, 2004, 30: 2117–2120.[8] Aygul Yeprem H. Effect of iron oxide addition on the hydration resistance and bulk density of doloma[J]. Journal of the European Ceramic Society, 2007,27: 1651–1655.[9] 程树江,程继健等. 铁钛复合添加剂对提高合成镁钙砂抗水化性的研究[J]. 华东理工大学学报,2000,2(26): 165-167.[10] 杨为振,陈树江等. Al2O3加入量对烧成镁钙砖性能的影响[J]. 鞍山科技大学学报,2003,6(26 ): 425-428.[11] 于燕文,杨正方等. 锆英石加入物对高钙MgO-CaO材料结构与性能的影响[J]. 稀有金属材料与工程,2005(34): 230-232.[12] 袁聪,赵惠忠等. 铁红对白云石熟料烧结性和抗水化性的影响[J]. 耐火材料,2011,4(45): 265-267.[13] 张汪年,邓宁等. CuO对白云石烧结性能的影响[J].粉末冶金技术, 2016,4(34): 277-280.[14] Aygul Yeprem H. Effect of Iron Oxide Addition on the Hydration Resistance and Bulk Density of Doloma[J]Journal of the European Ceramic Society,2007,27: 1651-1655.[15] 游杰刚,张国栋等. 二氧化硅对锆酸钙材料结构及性能的影响[J]. 人工晶体学报, 2014,5(43):1280-1285.