Abstract:SiCp/Al-Si composite with CeO2 addition was fabricated by powder metallurgy. The effect of CeO2 content on microstructure of the composite was investigated. The effects of CeO2 on the Si precipitation mechanism during sintering was also discussed. The results show that CeO2 can effectively refine the average size of precipitated silicon and increase its quantity. The optimum mass percent of CeO2 is 0.6%. Higher or lower CeO2 content will reduce the refining effects. As the heterogeneous nucleation substrate of precipitated silicon, CeO2 can improve the silicon nucleation rate, thus refine the precipitated silicon size and increase its precipitation quantity.