复层铁基粉末冶金材料的制备及其摩擦学性能分析
刘振明，尹延国，张国涛，尹利广
合肥工业大学摩擦学研究所， 安徽 合肥 230009
Preparation of iron-based powder metallurgy multi-layer material and its tribological performance analysis
LIU Zhen-ming，YIN Yan-guo，ZHANG Guo-tao，YIN Li-guang
Institute of Tribology， Hefei University of Technology， Hefei 230009， China
摘要 采用粉末冶金工艺制备基体致密、表层多孔含油的双层复合铁基粉末冶金材料，用HDM-20端面摩擦磨损试验机评价其摩擦磨损性能。结果表明，当复层材料表层的孔隙率约为23%时，试样稳定运行时间长，减摩耐磨性能好；与相近孔隙率的单层材料相比，复层材料的减摩耐磨性能与承载能力得到明显提高。
关键词 ：
粉末冶金 ,
复层材料 ,
高密度 ,
孔隙率 ,
摩擦磨损
Abstract ：Double layer iron-based composite material with dense matrix and porous oil-bearing surface was prepared by powder metallurgy method. The friction and wear properties were investigated on an HDM-20 tribo-tester. The results show that when the porosity of surface is about 23%， the sample has long stable operation time， good friction-reducing and wear-resistance performance. Compared with single layer sample with similar porosity， the multi-layer samples have obvious improvement on anti-friction and wear resistance performance， as well the bearing capacity.
Key words ：
powder metallurgy
multi-layer material
high density
porosity
friction and wear
收稿日期: 2015-06-08
出版日期: 2016-04-20
基金资助: 高性能液压泵关键摩擦副高强铁基减摩材料开发
通讯作者:
刘振明
E-mail: 1094760473@qq.com
[1]
邱 慧，班新星，刘建秀. SiC晶须含量对镁基复合材料性能影响的研究
[2]
高 远，朱 刘. 热压烧结P型碲化铋基热电材料的显微组织与性能
[3]
Dvid Whittker. 2015欧洲粉末冶金大会的金属增材制造：高温合金、粉末雾化、喷墨和激光金属沉积工艺的进展
[4]
钟海林，陈飞熊，李小明，况春江，王学兵，. 粉末冶金高速钢AHPT15M中碳化物的变化规律研究
[5]
冯 威，孔清泉，朱晓东，孙 艳，张永强. 添加升华性造孔剂的放电等离子法制备多孔铝块体材料
[6]
王天国，梁启超，覃 群. Al2O3含量对铜基粉末冶金摩擦材料摩擦磨损性能的影响
[7]
许恩恩，范慧俐，郭志猛，张乐美. 硅灰石纤维与二硫化钼填充改性聚四氟乙烯复合材料的性能研究
[8]
谷文金. 粉末冶金汽车DCT同步器齿毂在生产中的问题及解决方案
[9]
王荣旗，谢敬佩，吴文杰，王爱琴. CeO2对SiCp/Al-Si复合材料中析出Si影响机理的研究
[10]
王晓阳 ，茹红强. Cu-Fe基粉末冶金闸片制动特性的研究
[11]
于朝清，易 立，刘雪梅，任小梅，何小林，何 娇. WC材料和器件强韧化的工艺技术研究
[12]
曾昭锋. 多元陶瓷增强铜基复合材料的摩擦磨损性能
[13]
韩凤麟. 粉末冶金零件生产用润滑剂的性能改进与选择
[14]
刘汉强，赵 鹏，浦玉萍，沈 伟，朱黎冉. 孔密度和孔隙率对泡沫铜换热性能的影响
[15]
牟 楠，雷龙林，徐 然，唐 琳，罗丰华. 微细Cr-Fe合金粉对粉末冶金钢组织与性能的影响
2016, Vol. 26 