Abstract:The HVOF spraying parameters of CoCrW coating were optimized by using four factors and three levels orthogonal test method, the microstructure of coating was taken as objective to analyse the results and the adhesion strength of coating with substrate prepared by using optimized parameters were tested. The results show that the best process parameters is 897 L/min for the oxygen flow, 22 L/h for the kerosene flow, 66 g/min for the feed rate and 340 mm for the spray distance. The adhesion strength of CoCrW coating with substrate is 69.7 MPa at these parameters. The analysis shows that in HVOF spraying process, high-speed moving particles impact the matrix to produce shot peening effect. At the same time, kinetic energy is converted into thermal energy in a short time, which makes molten particles produce secondary plasticization at the interface. It is beneficial to the rapid spreading of the molten droplets, enhances the compactness of the coating and improves the bonding strength between the coating and the substrate.
吕艳红,张启富. HVOF喷涂CoCrW涂层的工艺参数优化及涂层显微组织对结合强度的影响[J]. , 2018, 28(04): 31-36.
Lü Yan-hong,ZHANG Qi-fu. The HVOF spraying parameters optimization of CoCrW coating and the effects of microstructure on adhesion strength. , 2018, 28(04): 31-36.
[1] Samit Kapoor. High-Temperature Hardness and Wear Resistance of Stellite Alloys[D]. Carleton University,Master of Applied Science, 2012:17-30.[2] S.M. GAYTAN, L.E. MURR, E. MARTINEZ, etal. Comparison of Microstructures and Mechanical Properties for Solid and Mesh Cobalt-Base Alloy Prototypes Fabricated by Electron Beam Melting[J].Metallurgical and meterials teansactions A,2010,41A,3216-3227.[3]Alireza Khoddamzadeh. Development of Carbon Fiber Reinforced Stellite Alloy Based Composites for Tribocorrosion Applications[D]. Doctor of Philosophy, Carleton University Ottawa,June, 2012, 14~17.[4]A.Farnia, F.Malek Ghaini, J.C.Rao, etal. Effect of Ta on the microstructure and hardness of Stellite 6 coating deposited by low power pulse laser treatments[J].Surface & Coatings Technology,2012,213,278~284.[5]徐锐. 航空发动机涡轮叶片锯齿冠耐磨涂层高温磨损性能研究[D].武汉理工大学硕士学位论文,2014:1~8.[6]孙勇汉,张斌,陈礼顺.航空发动机涂层技术研究及进展[J].航空制造技术,2013,(9):84-87.[7] 王璐. 热喷涂技术在先进航空发动机上的应用及前景展望[J].有色金属(冶炼部分),2008,增刊:7-9.[8] D.GUPTA, B.L.MORDIKE, S.SHARIFF, ETAL. Laser Surface Cladding of EN19 Steel with Stellite 6 for Improved Wear Resistance[J]. Lasers in Eng,2010,19:317-330.[9] YUCEL BIROL,AGCA B.KAYIHAN. Thermal Fatigue Testing of Plasma Transfer Arc Stellite Coatings on Hot Work Tool Steels under Steel Thixoforming Conditions[J]. METALLURGICAL AND METERIALS TRANSACTIONS A, 2011,42A,3277-3282.[10] H.Singh, B.S.Sidhu, D.Puri,etal. Use of plasma spray technology for deposition of high temperature oxidation/corrosion resistant coatings-a review[J].Materials and Corrosion,2007,58(2):92-102.[11]Chen,C J ,Wang, M C,Wang, D S,etal. Characterisations of electrospark deposition Stellite 6 alloy coating on 316L sealed valve used in nuclear power plant[J]. Materials Science and Technology, 2010, 26: 276~280.[12]华绍春,王汉功,汪刘应等.热喷涂技术的研究进展[J]. 金属热处理,2008,33(5):82-87.[13]H.Singh, B.S.Sidhu, D.Puri,etal. Use of plasma spray technology for deposition of high temperature oxidation/corrosion resistant coatings-a review[J].Materials and Corrosion,2007,58(2):92~102.[14] T.S.Sidhu,S.Prakash,R.D.Agrawal. STUDIES ON THE PROPERTIES OF HIGH-VELOCITY OXY-FUEL THERMAL SPRAY COATINGS FOR HIGHER TEMPERATURE APPLICATIONS[J].Materials Science, 2005,41(6):805-823.[15]S.Paul, M.D.F.Harvey. Corrosion Testing of HVOF Coatings in High Temperature Environments for Biomass Applications[C]. International Thermal Spray Conference & Exposition(ITSC)2012:403~407.[16]S.Houdkova, M.Kasparova, Z Cesanek. Wear resistant HVOF coatings for high temperature applications[C]. International Thermal Spray Conference & Exposition (ITSC), 2014: 506-512.[17]Sheng Hong, Yuping Wu, Yugui Zheng, etal. Effect of Spray Parameters on the Corrosion Behavior of HVOF Sprayed WC-Co-Cr Coatings [J]. Journal of Materials Engineering and Performance, 2014,23(4): 1434-1439.[18]M. Taheri, Z. Valefi and K. Zangeneh-Madar. Influence of HVOF process parameters on microstructure and bond strength of NiCrAlY Coatings [J]. Surface Engineering 2012, 28(4) 266-271.[19]吴子健,吴朝军,曾克里,等.热喷涂技术与应用[M].北京,机械工业出版社,2005.18-19.[20]J.Y.Cho, S.H.Zhang, T.Y.Cho. The processing optimization and property evaluations of HVOF Co-base alloy T800 coating[J].Journal Materials Science,2009,44:6348~6355.[21]Tillmann, W., Baumann, I. , Hollingsworth, P. ; Dildrop, M. etal. Influence of the handling parameters on the characteristics of Hvof sprayed coatings processed by means of fine WC-12Co (2-10μm) powders[C]. International Thermal Spray Conference & Exposition (ITSC), 2014: 324-332.[22] C.Lyphout, P.Nylen, L.Ostergren, et al. Relationships between Process Parameters, Microstructure and Adhesion Strength of HVOF Sprayed IN718 Coatings[C]. International Thermal Spray Conference & Exposition (ITSC), 2010: 476-481.[23] S. Kamis a, S. Gua, Numerical modeling the bonding mechanism of HVOF sprayed particles[J]. Computational Materials Science 46,2009:1038-1043.[24] 黎樵燊,朱又春.金属表面热喷涂技术[M].北京,化学工业出版社,2009:15-17.