Application and prospect of powder metallurgy in automobile |
GAO Yang, XU Yue-feng, TIAN Jie-ping |
(Dong Feng Peugeot Citroen Automobile Company Ltd., Wuhan 430056, China) |
|
|
Abstract Powder metallurgy materials are successfully applied for industrialized automobile parts, which broaden their application channels and reduce vehicle cost. The powder metallurgy materials, manufacturing processes and testing items were introduced, the performance requirements of powder metallurgy materials made for automobile parts were described, and some typical application examples were listed. For example, the MA manual transmission gear prepared by F50-N2U2-68 has a density of 6.8 g/cm3 and a hardness of 139 HV5. The key technology is that the gear ring is laser welded to the steel gear seat and then subjected to carbonitriding quenching. After heat treatment, the hardness is (390±70) HV5 and the crushing force is up to 10 780 N, meeting the requirement of a minimum breaking moment of 3 000 N·m, achieving a technical cost reduction of more than 4 million RMB per year. The exhaust valve seat of the engine prepared by the double-layer powder metallurgy material and copper melt leaching process has a porosity of 10%-15% and wear loss of less than 5 μm after 500 h durability test, which can save the cost of 20 RMB per car by replacing the original expensive high alloy elements (including Cr, Mo, W, V, Co, etc.).
|
Received: 15 May 2017
Published: 24 December 2018
|
|
|
|
[1]刘道春.汽车零部件的粉末材料技术及其发展[J].柴油机设计与制造, 2011, 17(1):11-11
[2] GB/T 3489-2015 硬质合金 孔隙度和非化合碳的金相测定[S].
[3] 黄伯云.粉末冶金标准手册(下册) 检验标准[M].中南大学出版社, 2000, :-
[4] 李绍忠.我国汽车用粉末冶金结构零件的发展[J][J].汽车研究与开发, 1996, (4):9-9
[5]刘东华, 钱晓泰.汽车铁基粉末冶金零件新进展[J].金属材料与冶金工程, 2013, 41(4):53-54
[6] 由粉冶材料齿环与钢材料齿轮本体结合的汽车变速箱齿轮的加工方法[P].中国专利: CN 102091920 A.
[7]毛志强.粉末冶金在汽车上的应用[J].粉末冶金工业, 2003, 13(1):9-9
|
|
|
|