多元陶瓷增强Cu基复合材料的导热性能研究

doi:10.13228/j.boyuan.issn1006-6543.20160011

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract The powder metallurgy vacuum hot-pressed sintered technology was used to prepare SiC， Si3N4， B4C multivariate ceramics/Cu composite. The thermal conductivity of the composite at room temperature was tested through laser pulse method. Results show that the thermal conductivity of the composite decreases gradually with the content increase of SiC， Si3N4， B4C multivariate ceramics， especially when the mass percent of the ceramic is more than 15.0%. Pores， grain boundary， lattice distortion， dislocation and other defects are the main factors that affect the thermal conductivity of the composite. To obtain composite materials with good thermal conductivity， the mass percent of multivariate ceramics particles should be controlled below 15.0%. Moreover， annealing or two times extrusion can be used to improve the density and reduce internal defects of the composite， thus increase the thermal conductivity.

Key words： Keywords Multivariate Ceramics/Cu composite powder metallurgy vacuum hot-pressed sintered technology thermal conductivity porosity interior defect.

Received: 15 February 2016 Published: 28 March 2017

Corresponding Authors: Zhaofeng Zeng E-mail: 524760608@qq.com

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZENG Zhao-Feng

Cite this article:

ZENG Zhao-Feng. Study on thermal conductivity of multivariate ceramics/Cu composite[J]. , 2017, 27(01): 42-47.

URL:

http://edit.chinamet.cn/Jweb_fmyjgy/EN/10.13228/j.boyuan.issn1006-6543.20160011 OR http://edit.chinamet.cn/Jweb_fmyjgy/EN/Y2017/V27/I01/42