Abstract：The effect of additive content on particle size and shrinkage rate was introduced in the process of producing permanent ferrite. The experiment shows that with the increase of the content of compound additives, the particle size of slurry is gradually reduced under the same condition of other experimental conditions. Along with the increase of the content of the additive, the axial shrinkage rate increases gradually, and the radial shrinkage decreases and then tends to be stable.
收稿日期: 2016-06-22
出版日期: 2016-11-04
通讯作者:
赵修彬
E-mail: zxb19871006@163.com
引用本文:
赵修彬 邱伟国 李劲松 舒云峰 马宝 李小艳. 添加剂对永磁铁氧体收缩率参数的影响[J]. , 2016, 23(5): 48-50.
ZHAO Xiu-bin, QIU Wei-guo, LI Jin-song, SHU Yun-feng, MA Bao, LI Xiao-yan. Study on effects of additives on the shrinkage rate parameters of permanent magnetic ferrites. , 2016, 23(5): 48-50.
[1] J. P. Jakubovics. Magnetism and Magnetic Materials [M]. The Institute of Metals, London: 1987.[2] M.M. Hessien, M.M. Rashad, M.S. Hassan, K. El-Barawy. Synthesis and magnetic properties of strontium hexaferrite from celestite ore[J]. J. Alloys Compd., 2009, 476: 373-378.[3] 王自敏 谢瑞兵等，添加剂对永磁铁氧体磁性能的影响研究[J]，中国陶瓷工业，2009（6）18-20。[4] 王自敏，邓志刚等 粒度及其分布对永磁铁氧体性能参数的影响规律研究[J]，中国陶瓷，2016（2）26-31.[5] 杨国本等，高性能永磁铁氧体磁体内外径尺寸公差与控制[J]，磁性材料及器件，1994（01）.[6] 周文运，烧结永磁铁氧体[M]，绵阳:磁性材料及器件专业情报网，2003,30-180.
2016, Vol. 23 