1ATTL Advanced Materials Co.Ltd, Beijing 100094, China;2Sichuan Academy of Aerospace Technology,
Chengdu 610100, China;3China University of Labor Relations, Beijing 100048, China
Abstract:This paper takes 97W-2Ni-1Fe tungsten alloy for counterweight as the research object. The phenomenon
reappearance analysis and verification are carried out for the large dispersion of the mechanical properties of
the body sampling during the product reinspection process, which provides a reference for subsequent failure analysis
and quality control of tungsten alloy. The test results show that the sintering temperature is the fundamental reason
that affects the discreteness of the properties of the tungsten alloy material. As a result, the tungsten particles inside
the structure grow abnormally, the structure is uneven, the bonding layer becomes thicker, and the tensile
strength of the material decreases. Fractures are dominated by tungsten- tungsten interface separation, which is a
typical brittle fracture.
左伟,郭胤,杨林,张振,王新磊,孙晓霞. 97W-2Ni-1Fe高比重合金配重块力学性能离散性原因分析[J]. 粉末冶金工业, 2021, 31(03): 99-103.
ZUOWei,GUO Yin,YANG Lin,ZHANG Zhen,WANG Xinlei,SUN Xiaoxia. Analysis of the causes for the dispersion of mechanical properties of a tungsten
alloy counterweight. Powder Metallurgy Industry, 2021, 31(03): 99-103.